Abstract:Aluminum foam that is lightweight with high specific strength, high energy absorption and other characteristics can be used in aerospace, transportation, machinery manufacturing and other fields. The PCM method is usually used to prepare closed-cell aluminum foams. The microsized aluminum foams made by this process can solve the non-uniform pore structures caused by liquid drainage during the foaming process of large aluminum foams. The surface morphology and internal pore structure of microsized aluminum foams are affected by the quality of the precursor used for foaming. In this paper, foamable precursors were obtained via either hot rolling or hot extrusion and subsequently foamed. By analyzing the micromorphology and foaming process of the precursor, the influence of the technological method on the macroscopic pore structure of the final aluminum foam was studied. The results show that the aluminum powder particles in the precursor prepared with the hot rolling method had metallurgical bonding, and the outer surface was dense, with almost no porosity and holes in the interior. The microsized aluminum foam obtained after foaming was smooth in appearance, and the internal pore structure was round and uniform. The reason is that during the foaming process of microsize aluminum foam, the foaming agent was evenly distributed in the precursor of the hot rolling process because of its compact structure. During the foaming process, the decomposed gas of the foaming agent will not escape, and the evenly distributed foaming agent tends to nucleate in situ. In the process of rapid foaming, the pressure in the bubble is enough to resist the liquid drainage phenomenon caused by gravity, and the growth direction of the gas core is isotropic, which promotes the foam structure to be more rounded and uniform.

Preparation principle and compression properties of cellular Mg–Al–Zn alloy foams fabricated by the gas release reaction powder metallurgy approach

Fabrication of Mg-Al Alloy Foam with Close-Cell Structure by Powder Metallurgy Approach and Its Mechanical Properties

Fabrication of Cellular Zn–Mg Alloy Foam by Gas Release Reaction Via Powder Metallurgical Approach

Fabrication of Cu-Mg alloy foam with close pore structure by gas release reaction powder metallurgical approach

Low-Temperature Reactive Sintered Porous Mg-Al-Zn Alloy Foams

Reactive sintering principle and compressive properties of porous AZ91 magnesium alloy foams produced by powder metallurgy approach

Fabrication of Zn Alloy Foam Via Powder Metallurgical Approach

Optimization of Mg Blowing Agent Content for Foaming Aluminum

Effect of Cu and Sn Additions on the Cellular Structure of Al–Si–Mg Alloys Foaming at Low Temperature (≤600 °C)

Fabrication of Cellular Mg Alloy by Gas Release Reaction Via Powder Metallurgical Approach

Optimization of Cellular Structure of Aluminum Foams Produced by Powder Metallurgy Method

Effect of Heat Treatment on the Microstructure, Compressive Property, and Energy Absorption Response of the Al–Mg–Si Alloy Foams

Preparation Technology of Aluminum Foam Sandwich Panels by Powder Metallurgy and Optimization of Cellular Structure

Preparation and Compressive Performance of an A356 Matrix Syntactic Foam

Effect of Zinc Content on the Mechanical Properties of Closed-Cell Aluminum Foams

Foamability and mechanical properties of in situ submicron MgAl2O4p/Al composite foams by ultrasonic method

Fabrication of Al Foam Without Thickening Process Through Melt-Foaming Method

Development of AlMg35-TiH2 composite foaming agent and fabrication of small pore size aluminium foams

Controllable Design of Structural and Mechanical Behaviors of Al‐Si Foams by Powder Metallurgy Foaming

Influence of Gas Pressure and Blowing Agent Content on the Formation of Aluminum Alloy Foam

Foaming Behavior of Microsized Aluminum Foam Using Hot Rolling Precursor