Abstract:In this paper, a high-yield Hf-modified SiHfBOC ceramic precursor was developed, and a high-pressure assisted impregnation pyrolysis method was proposed to achieve the preparation of 3D PyC-C-f/SiHfBOC composites. This high-pressure assisted impregnation method significantly improves impregnation filling effect of the precursor in and between fiber bundles compared to dozens of traditional impregnation cycles. After undergoing just 9 precursor infiltration pyrolysis (PIP) cycles, the composites achieved relative density of approximately 90% and density of 1.64 g/cm(3). The critical temperature difference of the 3D PyC-C-f/SiHfBOC composites after the shock of room temperature (RT)-1000. is as high as 650 degrees C, which is twice that of traditional ceramic materials, showing good thermal shock resistance. Under the effect of Hf modification, a dense HfO2-SiO2 oxide layer (thickness of 93 mu m) was formed in situ on the surface of the 3D PyC-Cf/SiHfBOC composites, effectively preventing further erosion of the composite matrix by high-temperature oxidation gas. Even in the ultra-high-temperature oxygen-containing environment at 1800 degrees C, it still exhibits an excellent non-ablative result (with a linear ablation rate of 0.83x10(-4) mm/s). This work not only enriches the basic research on lightweight ultra-high-temperature ceramic composites converted from Hf ceramic precursors, but also provides strong technical support for their applications in ultra-high-temperature non-ablative thermal protection materials for high-speed aircraft.

Ablation behavior of a three-dimensional C/C-HfC composite prepared by a precursor infiltration and pyrolysis method

Ablation behavior of HfC coating with different thickness for carbon/carbon composites at ultra-high temperature

Microstructure and ablation behavior of C/C–HfC–SiC composites fabricated by reactive melt infiltration with Hf–Si alloy

Ablation behavior of 3D PyC-Cf/SiHfBOC Composites under an oxyacetylene torch environment above 2000 °C

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Cyclic ablation behavior of mullite-modified C/C-HfC-SiC composites under an oxyacetylene flame at about 2400 °C

Effect of PyC interface phase on the cyclic ablation resistance and flexural properties of two-dimensional Cf/HfC composites

Ablation Behavior of the SiC-Coated Three-Dimensional Highly Thermal Conductive Mesophase-Pitch-Based Carbon-Fiber-Reinforced Carbon Matrix Composite under Plasma Flame

Microstructure and ablation resistance of C/C-HfC-SiC composites prepared by RMI with different powder particle sizes

SiC Nanowires Toughed HfC Ablative Coating for C/C Composites

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Ablation behaviors of ultra-high temperature ceramic composites

Ultra-high temperature ablation behavior of CVD-Hf 5 TaC 6 solid solution ceramic coating for C/C composites: Experiment and first-principle calculation

Effect of HfC addition on ablation behavior of SiBCN ceramics

Comparative ablation behaviors of C/SiC–ZrC and C/SiC–HfC composites prepared by ceramization of carbon aerogel preforms

Efficient Fabrication of Light Cf/SiHfBOC Composites with Excellent Thermal Shock Resistance and Ultra-High-temperature Ablation Up to 1800 °C

Ablation Resistance of HfC(Si, O)-HfB2(Si, O) Composites Fabricated by One-Step Reactive Spark Plasma Sintering

Ablation mechanism and morphology evolution of the HfC-SiC coating for C/C composites deposited by supersonic atmospheric plasma spraying

UHTC coating reinforced by HfC nanowires against ablation for C/C composites

Ablation behavior of high-entropy boride (Hf-Zr-Ta-Ti)B 2 coating fabricated via supersonic atmospheric plasma spraying for carbon/carbon composites

Ablation behavior of mullite modified C/C-SiC-HfC composites under oxyacetylene torch for single and cyclic ablations with two heat fluxes