Crystallinity dependence of high-temperature oxidation of silicoboron carbonitride monoliths
Bin Liang,Qishuai Zhu,Xingqi Liao,Kangwei Liu,Zhihua Yang,Dechang Jia,Yu Zhou
DOI: https://doi.org/10.1016/j.corsci.2021.109473
IF: 7.72
2021-07-01
Corrosion Science
Abstract:<p>Comparative investigation of performances of metastable materials in amorphous and crystalline states is one of the keys to exploring their applications in engineering. The oxidation behavior and kinetics of the partially crystalline Si<sub>2</sub>BC<sub>3</sub>N (PCS) monoliths, i.e. amorphous Si<sub>2</sub>BC<sub>3</sub>N with precipitation of nanocrystallites (10-30 nm) of SiC and BN(C), were investigated at 1500-1700 °C with dwell time ranging from 0.5 h to 16 h. Oxidation leads to the formation of amorphous SiO<sub>2</sub> and cristobalite, and more sufficient crystallization of PCS. Due to the release of gases including CO, CO<sub>2</sub>, N<sub>2</sub> and evaporation of B<sub>2</sub>O<sub>3</sub>, PCS undergoes weigh loss at 1500-1700 °C. Loose oxide scales with low adhesion strength are formed at 1500-1600 °C, while the scales are highly dense, adherent at 1700 °C indicating good oxidation resistance of PCS. Compared to completely amorphous Si<sub>2</sub>BC<sub>3</sub>N (CAS), PCS exhibits lower activation energy of ∼50.0 kJ‧mol<sup>-1</sup> for 1500-1600 °C/≤16 h, and higher parabolic rate constants (42.5 μm<sup>2</sup>‧h<sup>-1</sup> for 1500 °C/≤16 h, 172.2 μm<sup>2</sup>‧h<sup>-1</sup> for 1600 °C/≤16 h, and 120.4 μm<sup>2</sup>‧h<sup>-1</sup> for 1700 °C/≤4 h), which suggests the inferior oxidation resistance of PCS. One most possible reason is that the changes in superficial chemical compositions and reactivity during crystallization cause larger oxygen uptake on PCS surfaces.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering