Abstract:Unraveling the varied modification mechanisms of trace elements under diverse cooling rates is of great importance to regulate the morphology of primary Mg 2 Si in hypereutectic Al-Mg 2 Si alloys. In the present work, the modification mechanisms of Sr and Sb in Al-20Mg 2 Si alloys under different cooling rates are discussed in detail. Increasing the cooling rates from ~ 50 to 76 °C/s to ~ 213 to 230 °C/s leads to the morphology transition of primary Mg 2 Si from hoppers to dendrites, which is attributed to a smaller constitutional zone with the increase of temperature gradients introduced by high cooling rates. The addition of 0.15 wt pct Sr modifies the morphology of primary Mg 2 Si phase to cubes at cooling rates of ~ 50 to 76 °C/s and ~ 213 to 230 °C/s with the same modification mechanism, i.e. , by increasing nucleation driving force for primary Mg 2 Si and the adsorption-poisoning effect. In contrast, the modification mechanisms of Sb are different under varying cooling rates. At low cooling rates of ~ 50 to 76 °C/s, Sb modifies the morphology of primary Mg 2 Si to be truncated octahedrons by introducing Mg 3 Sb 2 particles as heterogeneous nuclei and the substitution of Sb to Si in Mg 2 Si crystals. At high cooling rates of ~ 213 to 230 °C/s, primary Mg 2 Si grows coarser with a dendrite morphology due to solute trapping, which changes the modification mechanism to substitution alone. Moreover, it is interesting that at cooling rates of ~ 213 to 230 °C/s, primary and eutectic Mg 2 Si particles in the Al-20Mg 2 Si-0.15Sr alloy are refined simultaneously, which greatly suppresses the crack formation and propagation. Accordingly, the ultimate tensile strength and elongation to failure are increased to ~ 242 MPa and ~ 5.6 pct compared to the unmodified alloy (~ 188 MPa and ~ 1.4 pct, respectively).

Spheroidization of Primary Mg2si in Al-20mg(2)Si-4.5cu Alloy Modified with Ca and Sb During T6 Heat Treatment Process

The Effect of Solution Treatment on the Si Particles’ Morphology Evolution and the Thermal Conductivity and Tensile Properties of Sb-Modified Al-8Si-0.6Mg Alloys

One-Step Synthesis of Spherical Primary Mg2Si in Ca/Sb-Modified Al-Mg2Si Alloy

Heterogeneous nucleation of Mg2Si on CaSb2 nucleus in Al–Mg–Si alloys

Synergetic Modification Effects on Primary Mg2Si in Al-20Mg2Si Alloy Induced by the Co-Addition of Beryllium and Antimony

Morphology Evolution of Primary Mg2Si in Al–20Mg2Si–0.1Ca Alloys Prepared with Various Solidification Cooling Rates

Influence of Li2sb Additions on Microstructure and Mechanical Properties of Al-20mg(2)Si Alloy

Microstructural Evolution Behavior of Mg–5Si–1Al Alloy Modified with Sr–Sb During Isothermal Heat Treatment

Refinement and modification of primary Mg2Si in an Al–20Mg2Si alloy by a combined addition of yttrium and antimony

Varied Modification Mechanisms of Sr and Sb under Diverse Cooling Rates on Primary Mg 2 Si in an Al-20Mg 2 Si Alloy

Synthesis of octahedron and truncated octahedron primary Mg2Si by controlling the Sb contents

The Effect of Sb Addition on Microstructures and Tensile Properties of Extruded Al–20Mg2Si–4Cu Alloy

Varied Modification Mechanisms of Sr and Sb under Diverse Cooling Rates on Primary Mg2Si in an Al-20Mg2Si Alloy

Formation of Spheroidal Microstructure in Semi-solid State of Al-4.8Si-2.8Cu-0.5Mg Aluminium Alloy

Preparation of Mg-15%Al-5%Si-0.5%Sb Alloy and Its Microstructure

Influences of Morphology and Size of Mg2Si on Microstructural Evolution of Mg–6.2Si Alloys During Partial Remelting

Effects of Complex Modification by Sr–Sb on the Microstructures and Mechanical Properties of Al–18 Wt % Mg2Si–4.5Cu Alloys

Development of Spherical Eutectic Si Particles through M-SIMA Process and Its Effects on the Tensile Properties of Al-7Si-0.05Sr Alloy

Modification of Primary Mg2si in Mg-4si Alloys with Antimony

Regulative Effect of Mg/Si Ratio on Microstructure Evolution and Mechanical Properties of Cast Al-Li-Mg-Si Alloys