One-Step Synthesis of Spherical Primary Mg2Si in Ca/Sb-Modified Al-Mg2Si Alloy

Hong-Chen Yu,Nan Li,Di-Wen Jiang,Ji-Biao Han,Yong-Qi Gao

DOI: https://doi.org/10.1007/s11665-024-10203-4

IF: 2.3

2024-10-06

Journal of Materials Engineering and Performance

Abstract:One-step synthesis of spherical primary Mg 2 Si is achieved in 0.5 wt.% Ca/Sb-modified Al-12Mg 2 Si alloy by gravity casting for the first time. The addition of 0.5 wt.% Ca/Sb results in large number density of CaSb 2 compounds for the nucleation of primary Mg 2 Si. Embryos of primary Mg 2 Si can be formed on these CaSb 2 compounds in the hypereutectic areas caused by the composition fluctuations. Low content of Mg/Si reduces the Mg/Si concentration for the growth of primary Mg 2 Si, which results in the final particle size which is less than the critical size of primary Mg 2 Si isotropic growth; the spherical primary Mg 2 Si is formed. Fracture behavior changes from the transgranular fracture of eutectic Mg 2 Si to intergranular fracture of primary Mg 2 Si with the formation of primary Mg 2 Si in Al-12Mg 2 Si alloy. Formation of spherical primary Mg 2 Si decreases the stress concentration, while the bonding strength between the particle and matrix is enhanced. Ultimate tensile strength of 0.5 wt.% Ca/Sb-modified Al-12Mg 2 Si alloy is improved significantly (from ~ 168 to ~ 230 MPa). The study provides a simple methodology to prepare spherical primary Mg 2 Si, which is beneficial to improving the mechanical property of Al-Mg 2 Si alloy.

materials science, multidisciplinary