Abstract:Spark plasma sintering was employed to synthesize high-density bulk MoSi2 in one step, using Mo and Si element powders as starting materials. Influence of sintering temperature on sintering behavior and microstructures of MoSi2 were investigated. The sintering behavior at whatever temperature (1473, 1673 and 1873K) is characterized by four stages, i.e., initial expansion, slight shrinkage, abrupt shrinkage and slight expansion. The maximum shrinkage displacement increased with increasing sintering temperature. When the sintering temperature reaches 1673K or 1873K, the second phases, i.e., SiO2 and Mo5Si3/Mo4.8Si3C0.6, were uniformly distributed in the synthesized MoSi2 matrix accompanied with a small amount of porosity. Most of SiO2 and Mo5Si3/Mo4.8Si3C0.6 particles were concentrated at grain boundaries. The relative density of the products (atomic ratio: Mo/2.00Si) was improved tremendously from 89% to 98.2% over the range 1473–1673K, and much smaller enhancement up to 99.0% was achieved from 1673 to 1873K. At the same time, the grain size and amount of second phase particles (mainly Mo5Si3/Mo4.8Si3C0.6) consistently increased with increasing temperature over 1473–1873K. However, the use of a slight excess of Si (e.g., atomic ratio: Mo/2.06Si) at 1673K resulted in dense products of MoSi2 nearly free of Mo5Si3/Mo4.8Si3C0.6, with the relative density of 99.2% and the average grain size of 5–10μm. Thereby, in order to pursue an equilibrium among densification, microstructural refinement and formation of second phases, the most suitable sintering temperature and stoichiometry for fabrication of MoSi2 by SPS are recommended to be 1673K and a hyperstoichiometry of Mo/2.06Si in the present work.

Effect of In-Situ Formed MoSi2 on Phase Transformation and Thermal Diffusivity of Spark Plasma Sintered Silicon Nitride

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Effect of Mo Particle Size on Microstructure and Mechanical Properties of Spark Plasma Sintered Silicon Nitride

Study on Thermal Conductivity of Spark-Plasma-Sintered Silicon Nitride Ceramics

Effect of Multi-Sintering Additive MgO-Al2O3-CeO2 on Densification and Properties of Silicon Nitride Ceramics by Spark Plasma Sintering

Effect of Initial Phase Composition on the Phase Composition, Microstructure, and Mechanical Properties of Si3N4 Ceramics

Effect of Temperature on the Microstructures of In-Situ MoSi_2 Fabricated by Spark Plasma Sintering

Influence of Conductive Nano-Tic on Microstructural Evolution of Si3n4-Based Nanocomposites in Spark Plasma Sintering

Influence of Spark Plasma Sintering Temperature on Sintering Behavior and Microstructures of Dense Bulk MoSi2

Sintering of β-Si_3N_4 Powder and Thermal Conductivity of the Ceramic

Sintering of beta-Si3N4 Powder and Thermal Conductivity of the Ceramic

In Situ Synthesis of (Mo,Cr)Si2 Composites by Spark Plasma Sintering

In-situ Preparation of Nano MoSi 2 SiC Composite by Melt Infiltration of Silicon Method

Effect of MgF2 addition on mechanical properties and thermal conductivity of silicon nitride ceramics

Effect Of Microstructural Modification On Thermal Conductivity And Strength Of Silicon Nitride

Study Of The Comparative Effect Of Sintering Methods And Sintering Additives On The Microstructure And Performance Of Si3n4 Ceramic

Study on In-Situ Reaction Synthesis and Mechanical Properties of Si2N2O Ceramic

Structure and Properties of Spark Plasma Sintered SiC Ceramics with Oxide Additives

Fabrication, microstructure, and properties of SiC/Al4SiC4 multiphase ceramics via an in-situ formed liquid phase sintering

Comparative Study of Fluoride and Non-Fluoride Additives in High Thermal Conductive Silicon Nitride Ceramics Fabricated by Spark Plasma Sintering and Post-Sintering Heat Treatment