Abstract:In this study, structural, morphological, thermal and magnetic properties of amorphous-nanocrystalline Fe 70 Cr 10 Nb 10 B 10 (at.%) alloy are discussed. The formation and evaluation of amorphous-nanocrystalline structures of the alloy were followed by XRD, SEM-EDX, TEM, DTA, and VSM techniques. After 50 h of milling Cr, Nb, and B were completely dissolved into the Fe lattice forming 82% of the amorphous phase of the alloy. A gradual dissolution of the alloying elements also increased the lattice parameters concurrently. The lattice parameters reached a maximum value of 2.908 Å after 20 h of milling and then leveled off to a value of 2.891 Å at the end of 50 h of milling. Based on the XRD data, crystallite size and lattice strain of the alloy were calculated as 3.2 nm and 3.34% respectively. TEM analyses revealed that the alloy particulates comprised needle-shaped nanoparticles of an average size of 21 nm. The room temperature magnetic hysteresis loops showed that the increased duration of milling decreased the saturation magnetization from 91 to 24 emu/g. This was mainly due to the upsurge on the amorphous phase content in the alloy as the milling progressed. The increase in amorphous phase content and the subsequent reduction of the saturation magnetization were due to the inter-diffusion of the non-ferromagnetic Cr and B atoms into the Fe lattice. Thermal studies revealed that around 350 °C the amorphous phase of the alloy began crystallizing. The magnetic saturation of the heat-treated alloy also increased with the growth in the crystalline phases. The 50 h milled sample annealed at 700 °C was found to have the highest magnetic anisotropy as observed from the temperature-dependent zero-field cooled and field cooled magnetization measurements. The high-pressure X-ray diffraction measurements revealed that the amorphous state of the alloy remained stable up to 11.3 MPa. It also revealed the structural similarities of the Fe 70 Cr 10 Nb 10 B 10 alloy with those of the Fe 70 M 10 B 20 (M = Nb and Cr) types. For all practical purposes, the microstructural stability under high compressive pressure represents the consolidation properties of the nanostructured magnetic materials since both pressure and temperature-induced phase transformations are the primary controlling factors for the specific magnetization properties of the alloy.

Preparation of Nanocrystalline Fe83Nb7B9Cu1 Powders by Mechanical Alloying and Their Thermal Stability

Preparation of Nb3al by High-Energy Ball Milling and Superconductivity

Nanocrystalline/Amorphous Tuning of Al–Fe–Nb (Mn) Alloy Powders Produced via High-Energy Ball Milling

Crystallization Kinetics and Magnetic Properties of Fe73.5si13.5b9cu1nb1v2 Nanocrystalline Powder Cores

Fabrication of nanocrystalline supersaturated W–Al alloys with enhanced thermal stability and high sinterability

Preparation of Nb 3 Al Superconductor by Powder Metallurgy and Effect of Mechanical Alloying on the Phase Formation

Synthesis and characterization of amorphous-nanocrystalline Fe70Cr10Nb10B10 powders by mechanical alloying

Formation of Nanocrystalline Fcc Phase by Mechanically Driven Crystallization

Crystallization Kinetics of Co-Finemet Amorphous Alloys and Magnetic Properties of Nanocrystalline Powder Cores

Effects of boron content on the structure and magnetic properties of Fe81-xSi13BxMo2Cr1Cu1P2 nanocrystalline alloys

Amorphization in the AlC System by Mechanical Alloying

Microstructural evolution and thermal stability in a nanocrystalline lightweight TiAlV0.5CrMo refractory high-entropy alloy synthesized by mechanical alloying

Evolution from Amorphous to Nanocrystalline and Corresponding Magnetic Properties of Fe-Si-B-Cu-Nb Alloys by Melt Spinning and Spark Plasma Sintering

Preparation and Electromagnetic Absorption Properties of Fe73.2Si16.2B6.6Nb3Cu1 Nanocrystalline Powder

Mechanical Alloying, Fine Structure and Thermal Decomposition of Nanocrystalline Fcc-Fe60cu40

Study on mechanical alloying behavior and thermal stability of HfMoNbTaTi refractory high-entropy alloy

Structural and thermal properties of the Fe-based alloys prepared by mechanical milling

Quantitative Crystallization and Nano-Grain Size Distribution Studies of a Fecunbsib Nanocrystalline Alloy

Effect of Milling Parameters on the Development of a Nanostructured FCC–TiNb15Mn Alloy via High-Energy Ball Milling

Preparation of FeAl (B2) intermetallic powder by ball milling and heat treatment

Effects of annealing temperature and heating rate on microstructure, magnetic, and mechanical properties of high-Bs Fe81.7−xSi4B13NbxCu1.3 nanocrystalline alloys