Nanocrystalline/Amorphous Tuning of Al–Fe–Nb (Mn) Alloy Powders Produced via High-Energy Ball Milling
Nguyen Thi Hoang Oanh,Dao Truong An,Nguyen Hoang Viet
DOI: https://doi.org/10.3390/ma17225627
IF: 3.4
2024-11-27
Materials
Abstract:The demand for advanced Al-based alloys with tailored structural and magnetic properties has intensified for applications requiring a high thermal stability and performance under challenging conditions. This study investigated the phase evolution, magnetic properties, thermal stability, and microstructural changes in the Al-based alloys Al82Fe16Nb2 and Al82Fe14Nb2Mn2, synthesized via mechanical alloying (MA), using stearic acid as a process control agent. The X-ray diffraction results indicated that Al82Fe16Nb2 achieved a β-phase solid solution with 13–14 nm crystallite sizes after 5 h of milling, reaching an amorphous state after 10 h. In contrast, Al82Fe14Nb2Mn2 formed a partially amorphous structure within 10 h, with enhanced stability with additional milling. Magnetic measurements indicated that both alloys possessed soft magnetic behavior under shorter milling times (1–5 h) and transitioned to hard magnetic behavior as amorphization progressed. This phenomenon was associated with a decrease in saturation magnetization (Ms) and an increase in coercivity (Hc) due to structural disorder and residual stresses. Thermal stability analyses on 10 h milled samples conducted via differential scanning calorimetry showed exothermic peaks between 300 and 800 °C, corresponding to phase transformations upon heating. Post-annealing analyses at 550 °C demonstrated the presence of phases including Al, β-phase solid solutions, Al13Fe4, and residual amorphous regions. At 600 °C, the Al3Nb phase emerged as the β-phase, and the amorphous content decreased, while annealing at 700 °C fully decomposed the amorphous phases into stable crystalline forms. Microstructural analyses demonstrated a consistent reduction in and homogenization of particle sizes, with particles decreasing to 1–3 μm in diameter after 10 h. Altogether, these findings highlight MA's effectiveness in tuning the microstructure and magnetic properties of Al–Fe–Nb (Mn) alloys, making these materials suitable for applications requiring a high thermal stability and tailored magnetic responses.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering