Abstract:Si3N4 ceramic with ultrafine fibrous grains are expected to exhibit remarkable mechanical properties. In this work, highly porous Si3N4 ceramic monoliths composed of ultrafine fibrous grains were developed via a novel vapor-solid carbothermal reduction nitridation (V-S CRN) reaction between SiO vapor and green bodies comprised of carbon nanotubes (CNTs), α-Si3N4 diluents and Y2O3 in a N2 atmosphere. The unique fibrous grains-interconnected structure was developed through in-situ formation of Si3N4 and following liquid phase sintering. The porous Si3N4 monoliths with porosity of 61–78% was developed by controlling the contents of α-Si3N4 diluents and densities of the CNT green bodies. With increasing of the α-Si3N4 contents, Si3N4 fibrous grains with an aspect ratio of approximate or higher than 20 could be achieved, and the grains were gradually refined. For the samples with 40 wt% α-Si3N4, the minimum mean grain diameter and pore size of 164 nm and 0.79 μm were achieved, respectively, and the resultant porous Si3N4 monolith exhibited a flexural strength of as high as 73–102 MPa with the porosity of 61–73%, which is much higher than that of the reported in literature. The improvement of mechanical strength could be attributed to the densely interconnected bird's nests structure formed by the ultrafine fibrous grains. The effects of the α-Si3N4 diluents on the resulting porous Si3N4 monolith via this method were analyzed.

Synthesis of Honeycomb-Like Structured Porous Si3n4 Ceramics with Exceptionally High Number of Cells Per Square Inch

Preparation of Porous Si3N4 Ceramics with Unidirectionally Aligned Channels

Manufacture of Si3N4-SiCN composite bulks with hierarchical pore structure

Fabrication of hierarchically porous Si3N4 foam ceramics with stamen-like cell structure

Microstructure and properties of porous Si3N4 ceramics by gelcasting-self-propagating high-temperature synthesis (SHS)

Preparation and properties of ultralight fibrous β-Si3N4 3D scaffolds with honeycomb-like structure by directional freeze-casting

Preparation and Pore Structure Characteristics of SiC Honeycomb Ceramics with Macroporous Walls

Preparation and properties of porous alumina with highly ordered and unidirectional oriented pores by a self-organization process

Porous Si3N4-based Ceramics with Uniform Pore Structure Originated from Single-Shell Hollow Microspheres

Pore Morphology Designs of Porous Si3n4-Based Ceramics Using Si3n4 and Al2o3 Poly-Hollow Microspheres As Pore-Forming Agents

3D Printing of Honeycomb Si3N4 Ceramic

Preparation of Al2O3-Si3N4 Porous Ceramics with a Cactus-Like Architecture for Potential Filters Applications

Synthesis of Fibrous Β-Si3n4 Structured Porous Ceramics Using Carbothermal Nitridation of Silica

Microstructure, Mechanical and Dielectric Properties of Highly Porous Silicon Nitride Ceramics Produced by a New Water-Based Freeze Casting

Morphology Design of Porous Si2N2O Ceramics via Silica Poly-Hollow Microspheres

Simultaneous improvement in porosity and strength of porous β-Si3N4 ceramics by formation of ultrafine fibrous grains

Facile Fabrication of Nanofibrous Network Reinforced Hierarchical Structured Porous Si3N4-based Ceramics Based on Si-Si3N4 Binary Particle-Stabilized Foams

From Bulk to Porous Structures: Tailoring Monoclinic SrAl2Si2O8 Ceramic by Geopolymer Precursor Technique

Novel porous Si3N4 ceramics prepared by aqueous gelcasting using Si3N4 poly-hollow microspheres as pore-forming agent

Preparation of Porous Si3N4 Ceramics with Controlled Porosity and Microstructure by Fibrous Α‐si3n4 Addition

Biomimetic Synthesis of Porous Si_3N_4 Ceramics