Abstract:Porous Si3N4 ceramics with bimodal hierarchical pore structures were fabricated through combining aqueous gelcasting and adding pore–forming agent method wherein a low–toxic monomer N, N–dimethylacrylamide (DMAA) and spherical pore–forming agent polystyrene sphere (PS) were respectively applied. The results demonstrated that PS size and content played an important function in regulating microstructure and properties of slurries, green and sintered bodies. The slurry viscosity increased sharply with the introduction of fine PS and reached a maximum of 1.78 Pa⋅s when adopting 7 wt% PS with d50 = 2.51 μm. Fine PS addition caused higher porosity in green bodies than coarse one, resulting in a significant reduction in bending strength from 28.50 MPa to 11.50 MPa, however, overall, demonstrating high enough strength for mechanical processing. The formed spherical pores from PS in ceramic matrix facilitated high porosity and highly crosslinked microstructure, thus contributing to lowering dielectric constant and loss. With PS size increasing, the dominant role in mechanical properties was transferred from porosity to microstructure, whilst dielectric properties were merely controlled by porosity and spherical pores. The porosity, bending strength, fracture toughness, dielectric constant and loss at 15 GHz varied in ranges of 36.34–52.91%, 258.42–101.21 MPa, 6.02–3.38 MPa⋅m1/2, 4.29–2.98 and 1.48–1.18 × 10−3, respectively, displaying an excellent comprehensive properties.

Manufacture of Si3N4-SiCN composite bulks with hierarchical pore structure

Formation of hierarchical Si3N4 foams by protein-based gelcasting and chemical vapor infiltration

Facile Fabrication of Nanofibrous Network Reinforced Hierarchical Structured Porous Si3N4-based Ceramics Based on Si-Si3N4 Binary Particle-Stabilized Foams

Porous Si3N4 ceramics with hierarchical pore structures prepared by gelcasting using DMAA as gelling agent and PS as pore–forming agent

SiC–Si3N4 composite with multi-laminate nanowires originated from oriented porous structure by freeze-casting

Three‐dimensional (3D) flexible nanofibrous network knitting on hierarchical porous architecture

Preparation, mechanical, dielectric and microwave absorption properties of hierarchical porous SiCnw-Si3N4 composite ceramics

Microstructure and properties of porous Si3N4 ceramics by gelcasting-self-propagating high-temperature synthesis (SHS)

Porous Si3N4-based Ceramics with Uniform Pore Structure Originated from Single-Shell Hollow Microspheres

Microstructure, Mechanical and Dielectric Properties of Highly Porous Silicon Nitride Ceramics Produced by a New Water-Based Freeze Casting

Synthesis of Honeycomb-Like Structured Porous Si3n4 Ceramics with Exceptionally High Number of Cells Per Square Inch

Pore Structure Control of Si3n4 Ceramics Based on Particle-Stabilized Foams

Novel porous Si3N4 ceramics prepared by aqueous gelcasting using Si3N4 poly-hollow microspheres as pore-forming agent

Microstructure and Properties of Porous Si3n4 Ceramics with A Dense Surface

Preparation and properties of ultralight fibrous β-Si3N4 3D scaffolds with honeycomb-like structure by directional freeze-casting

Simultaneous improvement in porosity and strength of porous β-Si3N4 ceramics by formation of ultrafine fibrous grains

Morphology Design of Porous Si2N2O Ceramics via Silica Poly-Hollow Microspheres

Si3N4 Hollow Microsphere Toughened Porous Ceramics from Direct Coagulation Method Via Dispersant Reaction

Ultralight and Mechanically Robust SiC Foams with Interconnected Cellular Architecture

Synthesis and Mechanical Properties of Highly Porous Ultrafine-Grain Si3N4 Ceramics Via Carbothermal Reduction-Nitridation Combined with Liquid Phase Sintering

A Novel Method of Strong and Tough Si3N4 Ceramic from the Particle‐stabilized Foam