Abstract:The pursuit of cost-efficiency, superior strength, and excellent gas permeance has driven the development of silicon carbide (SiC) membranes or filters for gas/solid filtration. In this study, SiC filters with high gas permeance reinforced with in situ- grown mullite whiskers were successfully prepared through reaction bonding. Low-cost kaolin and bauxite were used as sintering aids and raw materials for mullite whisker formation, and MoO 3 was used as an additive to promote mullite whisker growth. The effects of different sintering temperatures and the addition of kaolin, bauxite, and MoO 3 on filter performance were systematically investigated. When the sintering aid and MoO 3 content additions were 6 and 1.5 wt%, respectively, and the sintering temperature was 1450 °C, the resulting ceramic filter exhibited a porosity of 45.5 %, a bending strength of 17.9 MPa, and an average pore size of 47.7 μm. Moreover, the filter exhibited a high Darcy's permeability coefficient of 2.42 × 10 −11 m 2 , satisfactory chemical stability, and thermal shock resistance. The addition of MoO 3 facilitated the consumption of the molten phases and increased the anisotropic growth rate of the mullite whiskers, which contributed to the fabrication of the high-permeance filters. Finally, the ceramic filters demonstrated good performance for the filtration of dusty gases loaded with fly ash particles with a mean size of 15.3 μm at room temperature and 300 °C, and the removal rate reached > 99.9 %. The pressure drop was a little lower than that of our commercially available SiC filters. The SiC filters showed good prospects in the field of gas/solid filtration.

Preparation of Al2O3-Si3N4 Porous Ceramics with a Cactus-Like Architecture for Potential Filters Applications

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

Hierarchical Porous Ceramics with 3D Reticular Architecture and Efficient Flow-Through Filtration Towards High-Temperature Particulate Matter Capture

Preparation and enhanced mechanical properties of novel Al2O3‐C ceramic filter reinforced by microporous powder and SiC whiskers

Highly Porous SiC Cellular Ceramics for Efficient High-Temperature PM Removal

Hierarchical Ceramic Foams with 3D Interconnected Network Architecture for Superior High-Temperature Particulate Matter Capture

Ceramic foams with micron/sub-micron sized porous structure for efficient high-temperature particulate matter capture

Synthesis of Honeycomb-Like Structured Porous Si3n4 Ceramics with Exceptionally High Number of Cells Per Square Inch

Manufacture of Si3N4-SiCN composite bulks with hierarchical pore structure

Novel Design of Alumina Foams with Three‐dimensional Reticular Architecture for Effective High‐temperature Particulate Matter Capture

Process optimization of porous Al 2 O 3 filter via layered extrusion forming

Light-weight, wood-derived, biomorphic SiC ceramics by carbothermal reduction

Three‐dimensional (3D) flexible nanofibrous network knitting on hierarchical porous architecture

Fabrication of high-permeance SiC filters reinforced with in situ -grown mullite whiskers for gas/solid filtration

Facile Fabrication of Nanofibrous Network Reinforced Hierarchical Structured Porous Si3N4-based Ceramics Based on Si-Si3N4 Binary Particle-Stabilized Foams

Highly Porous and Hierarchical MgAl2O4 Ceramics with Improved Pore Connectivity Prepared from Gelled Particle-Stabilized Foams

Preparation of Porous Ceramic Support with Inorganic Filtration Membrane

Porous-foam mullite-bonded SiC-ceramic membranes for high-efficiency high-temperature particulate matter capture

Fabrication and Characterization of SiC-Based Porous Ceramic Used for High Temperature Filtration Supporter

Porous Si3N4-based Ceramics with Uniform Pore Structure Originated from Single-Shell Hollow Microspheres

SiC–Si3N4 composite with multi-laminate nanowires originated from oriented porous structure by freeze-casting