Abstract:We demonstrated a simple and effective approach to fabricate dense and high aspect ratio sub-50 nm pillars based on phase separation of a polymer blend composed of a cross-linkable polysiloxane and polystyrene (PS). In order to obtain the phase-separated domains with nanoscale size, a liquid prepolymer of cross-linkable polysiloxane was employed as one moiety for increasing the miscibility of the polymer blend. After phase separation via spin-coating, the dispersed domains of liquid polysiloxane with sub-50 nm size could be solidified by UV exposure. The solidified polysiloxane domains took the role of etching mask for formation of high aspect ratio nanopillars by O-2 reactive ion etching (RIE). The aspect ratio of the nanopillars could be further amplified by introduction of a polymer transfer layer underneath the polymer blend film. The effects of spin speeds, the weight ratio of the polysiloxane/PS blend, and the concentration of polysiloxane/PS blend in toluene on the characters of the nanopillars were investigated. The gold-coated nanopillar arrays exhibited a high Raman scattering enhancement factor in the range of 10(8)-10(9) with high uniformity across over the wafer scale sample. A superhydrophobic surface could be realized by coating a self-assembled monolayers (SAM) of fluoroalkyltrichlorosilane on the nanopillar arrays. Sub-50 nm silicon nanowires (SiNWs) with high aspect ratio of about 1000 were achieved by using the nanopillars as etching mask through a metal-assisted chemical etching process. They showed an ultralow reflectance of approximately 0.1% for wavelengths ranging from 200 to 800 nm.

Facile Synthesis of Silicon Micropillar Arrays Using Extreme Ultraviolet Lithography and Ag-Assisted Chemical Etching Method

Fabrication of Submicrometer Inp Pillars by Colloidal Lithography and Dry Etching

Optical Device Based on a Nanopillar Array by the Pattern Transfer of an Anodic Aluminum Oxide Membrane

Field Emission from a Periodic Amorphous Silicon Pillar Array Fabricated by Modified Nanosphere Lithography.

Wafer-Scale Fabrication of Ultra-High Aspect Ratio, Microscale Silicon Structures with Smooth Sidewalls Using Metal Assisted Chemical Etching

Enhanced Broadband Light Absorption in Silicon Film by Large-Size Lumpy Silver Particles

High aspect ratio arrays of Si nano-pillars using displacement Talbot lithography and gas-MacEtch

High Anti-Reflection Large-Scale Cup-Shaped Nano-Pillar Arrays via Thin Film Anodic Aluminum Oxide Replication

Fabrication of Silicon Hierarchical Nanopillar Arrays Based on Nanosphere Lithography

Size and Morphology Control of Highly-Ordered Nano-Silicon Pillar Fabricated by Direct Nanosphere Lithography

Formation of Nanostructured Emitter for Silicon Solar Cells Using Catalytic Silver Nanoparticles

Fabrication of large-scale periodic silicon nanopillar arrays for 2D nanomold using modified nanosphere lithography☆

An Innovative Light Trapping Structure Fabrication Method on Diamond-Wire-Sawing Multi-Crystalline Silicon Wafers

Carbon Nanotube Arrays for Optical Design of Amorphous Silicon Solar Cells

Fabrication of Ordered Arrays of Silicon Nanopillars at Selected Sites

Preparation of Hydrophobic/Superhydrophobic Surface on Silicon Wafer by Reactive Ion Etching and Self-assembled Monolayers

Fabrication of High-Aspect-ratio Silicon Nanopillar Arrays with the Conventional Reactive Ion Etching Technique

Wafer Scale Fabrication of Dense and High Aspect Ratio Sub-50 Nm Nanopillars from Phase Separation of Cross-Linkable Polysiloxane/Polystyrene Blend

FABRICATION OF SILICON NANOARRAYS BY DIRECT NANOSPHERE LITHOGRAPHY

Elliptical silicon arrays with anisotropic optical and wetting properties

Single Crystalline InGaAs Nanopillar Grown on Polysilicon with Dimensions beyond Substrate Grain Size Limit