Abstract:We demonstrated a simple and effective approach to fabricate dense and high aspect ratio sub-50 nm pillars based on phase separation of a polymer blend composed of a cross-linkable polysiloxane and polystyrene (PS). In order to obtain the phase-separated domains with nanoscale size, a liquid prepolymer of cross-linkable polysiloxane was employed as one moiety for increasing the miscibility of the polymer blend. After phase separation via spin-coating, the dispersed domains of liquid polysiloxane with sub-50 nm size could be solidified by UV exposure. The solidified polysiloxane domains took the role of etching mask for formation of high aspect ratio nanopillars by O-2 reactive ion etching (RIE). The aspect ratio of the nanopillars could be further amplified by introduction of a polymer transfer layer underneath the polymer blend film. The effects of spin speeds, the weight ratio of the polysiloxane/PS blend, and the concentration of polysiloxane/PS blend in toluene on the characters of the nanopillars were investigated. The gold-coated nanopillar arrays exhibited a high Raman scattering enhancement factor in the range of 10(8)-10(9) with high uniformity across over the wafer scale sample. A superhydrophobic surface could be realized by coating a self-assembled monolayers (SAM) of fluoroalkyltrichlorosilane on the nanopillar arrays. Sub-50 nm silicon nanowires (SiNWs) with high aspect ratio of about 1000 were achieved by using the nanopillars as etching mask through a metal-assisted chemical etching process. They showed an ultralow reflectance of approximately 0.1% for wavelengths ranging from 200 to 800 nm.

Fabrication of Submicrometer Inp Pillars by Colloidal Lithography and Dry Etching

Fabrication of InP nano pillars by ECR Ar ion irradiation

High aspect ratio arrays of Si nano-pillars using displacement Talbot lithography and gas-MacEtch

Size and Morphology Control of Highly-Ordered Nano-Silicon Pillar Fabricated by Direct Nanosphere Lithography

Fabrication and optical properties of silicon nanopillar arrays with controllable surface structures

Fabrication of High-Aspect-ratio Silicon Nanopillar Arrays with the Conventional Reactive Ion Etching Technique

Wafer Scale Fabrication of Dense and High Aspect Ratio Sub-50 Nm Nanopillars from Phase Separation of Cross-Linkable Polysiloxane/Polystyrene Blend

Fabrication Of Silicon Cones And Pillars Using Rough Metal Films As Plasma Etching Masks

Fabrication of the InP Nanopillars

Facile Synthesis of Silicon Micropillar Arrays Using Extreme Ultraviolet Lithography and Ag-Assisted Chemical Etching Method

A Facile Synthesis of Silicon Nanowires/micropillars Structure Using Lithography and Metal-Assisted Chemical Etching Method

Process optimization of inductively coupled plasma etching for large aspect ratio silicon nanopillars

Fabrication of Nanopillars Based on Silicon Oxide Nanopatterns Synthesized in Oxygen Plasma Removal of Photoresist

Single Crystalline InGaAs Nanopillar Grown on Polysilicon with Dimensions beyond Substrate Grain Size Limit

Large Area Fabrication of High Aspect Ratio Nano‐cylinders on Micro‐pillars Based on a Colloidal Crystal Mask

Formation of Silicon Nanopores and Nanopillars by A Maskless Deep Reactive Ion Etching Process

Fabrication of Ordered Arrays of Silicon Nanopillars at Selected Sites

Fabrication of silicon nanopillars containing polycrystalline silicon/insulator multilayer structures

Fabrication of Silicon Hierarchical Nanopillar Arrays Based on Nanosphere Lithography

Controlled thinning and surface smoothening of silicon nanopillars

Fabrication and Characterization of Slanted Nanopillars Array