Experimental Study on Three-Dimensional Deformation Field of Portevin–Le Chatelier Effect Using Digital Image Correlation

Y. Cai,Q. Zhang,S. Yang,S. Fu,Y. Wang

DOI: https://doi.org/10.1007/s11340-016-0138-1

IF: 2.794

2016-01-01

Experimental Mechanics

Abstract:In view of its high precision and high efficiency, three-dimensional digital image correlation (3D-DIC) is widely used to accurately measure full-field deformation. A spatiotemporal experimental study using 3D-DIC to explore the Portevin–Le Chatelier (PLC) deformational behavior, provides a new insight into the whole 3D deformation field, including the out-of-plane displacement, and in particular the relationship between the serrations and the strain field in the deformation bands corresponding to individual serrations. Specimens 1, 2 and 3 mm thick of 5456 Al-based alloy were tested in uniaxial tension at room temperature at strain rates from 1.8 × 10 −4 to 9.1 × 10 −3 s −1 . The spatial and temporal characteristics of the strain localization were quantitatively analyzed. The out-of-plane displacement increment field ( w ) of the localized bands was observed by 3D-DIC, and found to be related to the specimen thickness and the in-plane strain increment. The largest displacement increments were respectively 15, 10 and 5 μ m for 3, 2 and 1 mm specimens at maximum strain increment of about 12000 μ ε . The elastic shrinkage outside the deformation bands was found to be an essential characteristic of the PLC effect. The width of the PLC band ( w b a n d ) increased with increasing thickness; the angle of the PLC band ( 𝜃 b a n d ) was not affected by either specimen thickness or serration amplitude. Temporally, the serrations in the plots both of in-plane strain and out-of-plane displacement vs. time coincided throughout the entire loading procedure. When PLC banding occurred, the serration amplitude within the bands was found to be proportional to the maximum strain increment in the direction of the applied tensile force ( 𝜖 m a x ).