Abstract:The preparation of monolithic silica aerogels via non-supercritical drying is realized by the following procedures: (1) formation of silica alcogels with perfect network structure by controlling two-step hydrolysis and condensation reaction rates of tetraethoxysilane; (2) improvement and reinforcement of network structure and strength of silica gels through exchanging the pore fluid with ethanol solvent thoroughly, immersing of gels in the ethanol solutions of tetraethyoxysilane and aging; (3) gradual drying under ethanol fluid whose surface tension is much lower than water under ambient pressure. The resulting aerogels were characterized by means of SEM, TEM, TG-DTA, XRD, and adsorption-desorption techniques. It is found that the aerogels, which are made up of uniform spherical nanoparticles with diameters of about 10 nm, are of coherent network structures. Furthermore, the aerogels are porous, and the porosity is as high as 91%. The diameter of the pore sizes is in the range of 10 similar to 30 nm, and the density of the aerogels is low (200 similar to 400 kg . m(-3)). The specific surface area of the aerogels can be as high as 625. 65 m(2) . g(-1). The appearance, microstructure, diameters of primary particles and pore size distributions of the aerogels are in concordance with those prepared by conventional supercritical drying. It is demonstrated that the quality of the resulting aerogels is affected by the preparation conditions adopted in the preparation process. In fact, by adjusting the proportions of the reaction systems, and controlling the adding amounts of acid and base during the two-step hydrolysis and condensation process, silica aerogels with required density, definite strength and ideal morphology can be produced.

Microstructure Control of the Silica Aerogels Via Pinhole Drying

Preparation and Heat Treatment of Titania Aerogels by Ambient Pressure Drying

Preparation of Silica Aerogels Via Non-supercritical Drying and Their Formation Process

The Effects of Microstructure on Optical and Thermal Properties of Porous Silica Films

Preparation of Silica Aerogels by Non-Supercritical Drying

Application of Drying Control Chemical Additives in Preparation for Silica Aerogels

Preparation and characterization of monolithic TiO2/SiO2 aerogels obtained by non-supercritical drying method

Preparation of Methyltrimethoxysilane Derived Silica Aerogel Films via Ambient Pressure Drying

PREPARATION OF SILICA AEROGELS BY SUPERCRITICAL DRYING TECHNIQUE

Effect of the thermal treatment on microstructure and physical properties of low-density and high transparency silica aerogels via acetonitrile supercritical drying

Toward Improved Optical Transparency of Silica Nanofibrous Aerogels

Tailoring structure and properties of silica aerogels by varying the content of the Tetramethoxysilane added in batches

The control of shrinkage of silica aerogel at ambient pressure

The Relationship Between the Silica Wet-Gels Relative Optical Transmittance at 500 Nm and Structural Features of Silica Aerogels

Microstructure and Physicochemical Properties of Ambient-Dried SiO2 Aerogels with K2Ti6O13 Whisker Additive

Preparation and Characterization of Silica Aerogels from Diatomite Via Ambient Pressure Drying

Synthesis and Effect of DCCA on the Ambient Pressure Dried, TEOS-Based Silica Aerogel

Improvement of the Thermal Insulation Performance of Silica Aerogel by Proper Heat Treatment: Microporous Structures Changes and Pyrolysis Mechanism

Microstructural Characterization and Properties of Ambient-Dried Sio2 Matrix Aerogel Doped with Opacified Tio2 Powder

Effects of Surfactants on the Synthesis of Silica Aerogels Prepared by Ambient Pressure Drying

Synthesis and Characterization of Silica Aerogels Dried under Ambient Pressure Bed on Water Glass