Abstract:The preparation of monolithic silica aerogels via non-supercritical drying is realized by the following procedures: (1) formation of silica alcogels with perfect network structure by controlling two-step hydrolysis and condensation reaction rates of tetraethoxysilane; (2) improvement and reinforcement of network structure and strength of silica gels through exchanging the pore fluid with ethanol solvent thoroughly, immersing of gels in the ethanol solutions of tetraethyoxysilane and aging; (3) gradual drying under ethanol fluid whose surface tension is much lower than water under ambient pressure. The resulting aerogels were characterized by means of SEM, TEM, TG-DTA, XRD, and adsorption-desorption techniques. It is found that the aerogels, which are made up of uniform spherical nanoparticles with diameters of about 10 nm, are of coherent network structures. Furthermore, the aerogels are porous, and the porosity is as high as 91%. The diameter of the pore sizes is in the range of 10 similar to 30 nm, and the density of the aerogels is low (200 similar to 400 kg . m(-3)). The specific surface area of the aerogels can be as high as 625. 65 m(2) . g(-1). The appearance, microstructure, diameters of primary particles and pore size distributions of the aerogels are in concordance with those prepared by conventional supercritical drying. It is demonstrated that the quality of the resulting aerogels is affected by the preparation conditions adopted in the preparation process. In fact, by adjusting the proportions of the reaction systems, and controlling the adding amounts of acid and base during the two-step hydrolysis and condensation process, silica aerogels with required density, definite strength and ideal morphology can be produced.

Effects of Surfactants on the Synthesis of Silica Aerogels Prepared by Ambient Pressure Drying

Preparation of Silica Aerogels Via Non-supercritical Drying and Their Formation Process

PREPARATION OF SILICA AEROGELS BY SUPERCRITICAL DRYING TECHNIQUE

Preparation of Methyltrimethoxysilane Derived Silica Aerogel Films via Ambient Pressure Drying

Preparation and Surface Modification Mechanism of Silica Aerogels Via Ambient Pressure Drying

Preparation of Silica Aerogels by Non-Supercritical Drying

Preparation and characterization of monolithic TiO2/SiO2 aerogels obtained by non-supercritical drying method

A Novel Preparation of Superhydrophobic Silica Aerogels Via the Combustion Drying Method

Application of Drying Control Chemical Additives in Preparation for Silica Aerogels

Effects of Preparation Conditions on Hydrophobic Silica Aerogels Via Ambient Pressure Drying

Effect of Surface Modification Agents on Hydrophobiic, Elastic and Thermal Property of Silica Aerogels Derived from Ambient Condition

Effect of different types of surfactants on the microstructure of methyltrimethoxysilane-derived silica aerogels: A combined experimental and computational approach

Synthesis and Effect of DCCA on the Ambient Pressure Dried, TEOS-Based Silica Aerogel

Preparation of SiO2 aerogels with sol-gel method and the study of their properties

Ambient Pressure Preparation,Surface Structure and Adsorption Properties of Silica Aerogels

Enhancing Mesopore Volume and Thermal Insulation of Silica Aerogel via Ambient Pressure Drying-Assisted Foaming Method

Rapid Synthesis and Characterization of Ambient Pressure Dried Monolithic Silica Aerogels in Ethanol/water Co-Solvent System

Effect of different trimethyl silylating agents on the hydrophobic and physical properties of silica aerogels

Surfactant-free Synthesis of Silica Aerogel Microspheres with Hierarchically Porous Structure.

SiO 2 aerogels prepared by ambient pressure drying with ternary azeotropes as components of pore fluid

Preparation of Silica Aerogels Via Ambient Pressure Drying