Abstract:The preparation of monolithic silica aerogels via non-supercritical drying is realized by the following procedures: (1) formation of silica alcogels with perfect network structure by controlling two-step hydrolysis and condensation reaction rates of tetraethoxysilane; (2) improvement and reinforcement of network structure and strength of silica gels through exchanging the pore fluid with ethanol solvent thoroughly, immersing of gels in the ethanol solutions of tetraethyoxysilane and aging; (3) gradual drying under ethanol fluid whose surface tension is much lower than water under ambient pressure. The resulting aerogels were characterized by means of SEM, TEM, TG-DTA, XRD, and adsorption-desorption techniques. It is found that the aerogels, which are made up of uniform spherical nanoparticles with diameters of about 10 nm, are of coherent network structures. Furthermore, the aerogels are porous, and the porosity is as high as 91%. The diameter of the pore sizes is in the range of 10 similar to 30 nm, and the density of the aerogels is low (200 similar to 400 kg . m(-3)). The specific surface area of the aerogels can be as high as 625. 65 m(2) . g(-1). The appearance, microstructure, diameters of primary particles and pore size distributions of the aerogels are in concordance with those prepared by conventional supercritical drying. It is demonstrated that the quality of the resulting aerogels is affected by the preparation conditions adopted in the preparation process. In fact, by adjusting the proportions of the reaction systems, and controlling the adding amounts of acid and base during the two-step hydrolysis and condensation process, silica aerogels with required density, definite strength and ideal morphology can be produced.

Synthesis of Hydrophobic Silica Aerogels via Ambient Pressure Drying

Preparation of Silica Aerogels Via Non-supercritical Drying and Their Formation Process

Preparation and Characterization of Hydrophobic Silica Aerogel by Ambient Pressure Drying Method

Hydrophobic Silica Aerogels Prepared with Ambient Pressure Drying and the Adsorption Properties

Preparation of Methyltrimethoxysilane Derived Silica Aerogel Films via Ambient Pressure Drying

Preparation and Surface Modification Mechanism of Silica Aerogels Via Ambient Pressure Drying

Preparation of Silica Aerogels by Non-Supercritical Drying

Superhydrophobic Sodium Silicate Based Silica Aerogel Prepared by Ambient Pressure Drying

Synthesis and characterization of low density and hydrophobic silica aerogels dried at ambient pressure using sodium silicate precursor

Preparation of Hydrophobic SiO2 Aerogels at Ambient Pressure

Synthesis and Characterization of Silica Aerogels Dried under Ambient Pressure Bed on Water Glass

Hydrophobic Silica Aerogels Derived from Polyethoxydisiloxane and Perfluoroalkylsilane

Preparation of Flexible, Hydrophobic, and Oleophilic Silica Aerogels Based on a Methyltriethoxysilane Precursor

SiO 2 aerogels prepared by ambient pressure drying with ternary azeotropes as components of pore fluid

Synthesis and characterization of silica aerogels by a novel fast ambient pressure drying process

Preparation and Characterization of Silica Aerogels Derived from Ambient Pressure

Effects of Preparation Conditions on Hydrophobic Silica Aerogels Via Ambient Pressure Drying

SiO2 Aerogels Prepared with Ambient Pressure Drying and Its Properties

Facile Synthesis of Flexible and Hydrophobic Polymethylsilsesquioxane Based Silica Aerogel Via the Co-Precursor Method and Ambient Pressure Drying Technique

Silica Aerogels Having High Flexibility and Hydrophobicity Prepared by Sol-Gel Method

Preparation of Low Density Hydrophobic Silica Aerogels by Controlling Strength of Alcogels