Facile Synthesis of Flexible and Hydrophobic Polymethylsilsesquioxane Based Silica Aerogel Via the Co-Precursor Method and Ambient Pressure Drying Technique

Wu Xiaodong,Zhong Kai,Ding Jie,Shen Xiaodong,Cui Sheng,Zhong Ya,Ma Jiaying,Chen Xiangbao
DOI: https://doi.org/10.1016/j.jnoncrysol.2019.119826
IF: 4.458
2020-01-01
Journal of Non-Crystalline Solids
Abstract:The fragility, hydrophilicity and high cost fabrication of aerogels have limited their applications in industrial and civilian fields. Herein, we have described a method for preparing a novel flexible and hydrophobic silica aerogel by using the co-precursors method via ambient pressure drying technique. The optimal MTMS volume percentage is determined at 60%. The resulting aerogel obtains agglomerated particles with diameters at similar to 20-30 nm and mesopores at several tens of nanometers. The Si-C-H bond ratio maintains at 13. 36% after heat treatment at 300 degrees C, which results in the high water contact angle of 153.9 degrees. Moreover, the 300 degrees C heat treated aerogel has a much more homogeneous microstructure with its BET specific surface area as large as 895.5 m(2)/g. The oxidation peak of -CH3 groups is observed at 492 degrees C. The aerogel exhibits an excellent flexibility under 50 compression cycles, as well as a superior thermal insulation property.
What problem does this paper attempt to address?