Abstract:To further clarify the effect mechanism of MoS 2 element diffusion on tribological properties of cemented carbide materials, an investigation was carried in this study. The diffusion process between cemented carbide inserts and MoS 2 powder under high temperature condition was carried out in a muffle furnace device. The surface morphology and chemical element content of test samples were observed and measured with scanning electron microscope, energy spectrum, and X-ray diffraction instruments. The kinetics of the diffusion process was quantitatively discussed by thermodynamic experiments. Tribological experiments were carried out using friction and wear machine with which the friction coefficient and wear scar were obtained. The experimental results show that high temperature has a significant effect on physical and mechanical properties of cemented carbide materials. Moreover, MoS 2 elements diffusion on sample surface is existed and induced by thermal action, which results in a further changing of material properties of cemented carbide. The WC grain growth is inhibited when molybdenum element is only infiltration on sample surface at 500 °C, which improves the surface morphology and hardness of test sample. However, the oxidation rate, friction coefficient, and wear rate of test sample are the highest when heating temperature larger than 500 °C. The main reason is that, as the temperature increasing, the diffusion of sulfur elements is occurred and intensified the loss of cobalt element on sample surface. So, the bonding ability of it is decreased due to the loss of bonding phase Co. Thus, the surface hardness and wear resistance of test sample is deteriorated. This study provides a theoretical foundation for the application of molybdenum disulfide in tool cutting lubrication condition.

Effect of Ambient Temperature on Wear of Cemented Carbide Tool Material

Friction and Wear of Typical Tool Material at Elevated Temperature

Unlubricated Friction and Wear Behaviors of Al2O3/TiC Ceramic Cutting Tool Materials from High Temperature Tribological Tests

Friction and Wear Behaviors of Al<sub>2</sub>O<sub>3</sub> Based Ceramic Tool Materials at Temperatures up to 800°C

Analysis of High Temperature Wear Process Mechanism of Cemented Carbide Tool

Influences of different temperatures on the mechanical properties and wear resistance against Ti6Al4V of Ti doped diamond-like carbon deposited on cemented carbide

Effect of Temperature on Tribological Properties of Cu/Ti3AlC2 Composites

Inlfuences of Material Tool and Tool Wear on Cutting Temperature of Turning Titanium Matrix Composites

Effect of Temperature on the Friction and Wear Behaviors of Cr3C2–20 Wt% Ni Cermets

Preparation of Ultra-Fine ATC Ceramics and Analysis of Its Dry-Sliding Wear Behavior

Some Factors Affecting Wear on Cemented Carbide Tools

Research On Wear Behavior Of Atc Cermet Material

High-temperature mechanical properties of a cemented carbide cutter during extra-heavy cutting process

Wear Mechanisms of Cemented Carbide Tools in Dry Cutting of Precipitation Hardening Semi-Austenitic Stainless Steels

High temperature fracture mechanism of ultrafine WC-Co cemented carbides containing (Ti,W)C

Effect of Nickel Element Diffusion on the Tribological Properties of Cemented Carbide Materials under High Temperature Condition

Tribological Behavior and Wear Mechanism of Pure WC at Wide Range Temperature from 25 to 800 °C in Vacuum and Air Environment

Tribological Properties of Additive Manufactured Ti6Al4V Against Cemented Carbide under Dry Sliding Conditions

Effect of MoS 2 element diffusion under high temperature condition on the tribological properties of cemented carbide materials

INFLUENCE OF CARBIDE STABILITY ON WEAR RESISTANCE OF ALLOY AT ELEVATED TEMPERATURE

Temperature-induced wear transition in ceramic-metal composites