Evolution of the Microstructure and Mechanical Properties of As-Sprayed and Annealed Silicon Layer on Melt-Infiltrated Silicon Carbide Composites
Mengqiu Guo,Yongjing Cui,Chungen Zhou,Jian Jiao,Xiaofang Bi,Chunhu Tao
DOI: https://doi.org/10.2139/ssrn.4358387
2023-01-01
Abstract:Silicon coatings are the most extensively applied coatings as the bond layer for environmental barrier coatings (EBCs). In this study, silicon layers were deposited on melt-infiltrated SiC composites using atmospheric plasma spraying and then annealed at 1100 and 1250 °C for 1–10 h to investigate the effect of annealing on the layer. The microstructure and mechanical properties were evaluated using scanning electron microscopy, X-ray diffractometry, transmission electron microscopy, nano-indentation, and bond strength tests. A silicon layer with a homogeneous polycrystalline cubic structure was obtained without phase transition after annealing. Additionally, the silicon layer exhibited good oxidation resistance and the oxygen content in the cross-section did not exceed 3.5 wt%, which was significantly lower than that at the surface (45 wt%max). After annealing, three features were observed at the interface, namely, β-SiC/nano-oxide film/Si, Si-rich SiC/Si, and residual Si/nano-oxide film/Si. The nano-oxide film thickness was ≤ 100 nm and was well combined with SiC and silicon. Additionally, a good chemical bond was formed between the silicon-rich SiC and silicon layer, resulting in a significant bond strength improvement from 11 to > 30MPa. The hardness of the silicon layer increased by 22.6 and 16.7% after annealing at 1100 and 1250 °C, respectively, for 1 h, as compared to the original 11.83 GPa. Additionally, the dislocation density, which may contribute to the enhanced hardness, was examined and calculated using electron back-scatter diffraction.