Investigation of Ni/SiO 2 catalysts prepared at different conditions for hydrogen production from ethanol steam reforming

chunfei wu

DOI: https://doi.org/10.1016/j.joei.2016.01.002

IF: 6.47

2017-01-01

Journal of the Energy Institute

Abstract:Ni/SiO2 catalysts prepared by a sol–gel method have been investigated for hydrogen production via steam reforming of ethanol using a continuous flow, fixed bed reactor system. Chemical equilibrium calculations were also performed to determine the effects of temperature and molar steam to carbon ratio on hydrogen production. The acidity of the preparation solution (modified by nitric acid and ammonia) and calcination atmosphere (air and N2) were investigated in the preparation of the catalysts. BET surface area and porosity, temperature-programmed oxidation (TPO), X-ray diffraction (XRD), transmission electron microscopy (TEM) and scanning electron microscopy (SEM) were used to characterise the prepared catalysts. The BET surface area was reduced when the solution acidity was lowered during the sol–gel preparation process. A pH value less than 2.0 was necessary to achieve high metal dispersion in the catalyst. Smaller NiO particles were obtained when the catalyst was calcined in N2. Material balances on ethanol steam reforming at 600 °C using the prepared Ni/SiO2 catalysts were determined, and higher hydrogen production with lower coke deposition on the reacted catalysts were also obtained from the catalysts calcined in N2 atmosphere.