Abstract:The steam reforming of isooctane and methylcyclohexane (MCH) was investigated over Fe- and Ni-based catalysts. FeMg/Al2O3 catalyst, effective for CH4 decomposition in the presence of O2/CO2, was active for steam reforming of isooctane, being a little easier to cause C−C bond cleavage than MCH, but the rate of hydrogen production was insufficient, although the rate was only slightly improved by Rh modification, due to raised formation of CH4 and C2. FeMg/Al2O3 catalyst was also less active for the steam reforming of MCH than Ni systems. Modification of FeMg/Al2O3 catalyst with rhodium resulted in the increased formation of aromatic byproducts. The rate of H2 production with Ni/ZrO2 catalyst was found to be 7 times higher than that with FeMg/Al2O3. Furthermore, the stability of the Ni/ZrO2 catalyst was found to be improved by the addition of alkaline-earth metals into the catalyst (M/Ni = 1:2 wt ratio). In particular, the addition of Sr was the most effective and the activity of NiSr/ZrO2 catalyst for the reaction at 973 K remained stable after 100 hours, although below 10% decrease in the rate of H2 formation was observed. On the contrary, above 50% decrease in the rate was observed over Ni/ZrO2 catalyst, after 100 hours. This Sr effect, possibly, could be associated with the formation of mixed oxides consisting of Sr and Zr (or Ni). The NiSr/ZrO2 catalyst was also effective for the steam reforming of model gasoline, which contained organic mixtures with different reforming reactivities such as naphthenes, aromatics, and n- and iso-paraffins.

Steam reforming of ethanol for hydrogen production over NiO/ZnO/ZrO2 catalysts

Improvement of the stability of a ZrO2-modified Ni–nano-CaO sorption complex catalyst for ReSER hydrogen production

Sorption-Enhanced Steam Reforming of Glycerol for Hydrogen Production over a NiO/NiAl2O4 Catalyst and Li2ZrO3-Based Sorbent

Enhanced Hydrogen Production from Steam Reforming of Vegetable Oil over Bimodal ZrO2-SiO2 Supported Ni Catalyst

Catalytic Steam Reforming of Ethanol for Hydrogen Production over Ni/Ceo2-Zro2 Catalysts

Steam reforming of ethanol for hydrogen production: influence of catalyst composition (Ni/Al2O3, Ni/Al2O3–CeO2, Ni/Al2O3–ZnO) and process conditions

Steam reforming of ethanol with zirconia incorporated mesoporous silicate supported catalysts

Hydrogen Production by Steam Reforming of Ethanol over CuO-La_2O_3/ZrO_2 Catalyst

Hydrogen Production from Ethanol Steam Reforming over Ni/Al2O3 and Ni/La2O3 Catalysts at Low Temperature

STUDIES ON STEAM REFORMING OF METHANE OVER Ni/ZrO2 CATALYST

Studies on Ni/Al2O3 Catalyst for Hydrogen Production from Ethanol Steam Reforming

From Steam Reforming of Ethanol at Low Temperature over , and Catalysts for Fuel-Cell Application

Studies on CuO/La_2O_3-ZrO_2 Catalyst for Production of Hydrogen by Ethanol Steam Reforming

Methanol Steam Reforming over ZnO/ZnZrOx: Performance Enhanced with a Cooperative Effect

ZnO-ZnFe2O4 Catalyst for Hydrogen Production from Methanol Steam Reforming

Influences Of Reaction Conditions On Steam Reforming Of Methane Over Ni/Zro2 Catalyst.

Hydrogen Production Via Steam Reforming of Methanol on Cu/ZnO/Al2O3 Catalysts: Effects of Al2O3 Precursors

Steam reforming of ethanol over Cu/ZrO_2 catalysts II Influences of reaction conditions

Fe–Ni–Ce–Zr-modified CuO–ZnO catalyst for methanol steam reforming

Hydrogen Production from Steam Reforming of Hydrocarbons over Alkaline-Earth Metal-Modified Fe- or Ni-Based Catalysts

Hydrogen Production via Methanol Steam Reforming over CuO/ZnO/Al2O3 Catalysts Prepared via Oxalate-Precursor Synthesis