Abstract:<section class="article-section__content"><h3 class="article-section__sub-title section1"> BACKGROUND</h3>CO2 reforming of methane, also known as dry reforming of methane, has received significant attention because this technology can convert notorious greenhouse gases (CH4/CO2) into useful syngas (H2/CO). However, this technology still hasn't been commercialized, primarily due to the lack of feasible catalysts. </section><section class="article-section__content"><h3 class="article-section__sub-title section1"> RESULTS</h3>Based on zirconia (ZrO2) nanoparticles with pure monoclinic (m) or tetragonal (t) crystal phase, three nickel (Ni) catalysts (Ni/m‐ZrO2, Ni/t‐ZrO2 and Ni/m‐ZrO2@Al2O3) have been synthesized for CO2 reforming of methane. The Ni/t‐ZrO2 catalyst exhibited lowest reforming activity with CH4 conversion of 15.5% at 700 °C under 1 atm with a gas hourly space velocity (GHSV) of 96 000 mL/(h gcat). The Ni/m‐ZrO2 catalyst showed much higher initial activity but underwent severe deactivation, over which CH4 conversion decreased from 56.1% to 33.4% after 300 min of reaction. The nanocomposite Ni/m‐ZrO2@Al2O3 catalyst with confinement effect possessed the best activity and good stability. Specifically, its CH4 conversion decreased merely from 60.2% to 55.3% after 24 h of reaction. </section><section class="article-section__content"><h3 class="article-section__sub-title section1"> CONCLUSION</h3>Structural characterizations demonstrate that limited specific surface area and weak metal‐support interactions existed on the Ni/t‐ZrO2 catalyst, which led to large Ni nanoparticles and thus poor reforming activity. Both Ni/m‐ZrO2 and Ni/m‐ZrO2@Al2O3 catalysts had high specific surface area and tiny Ni nanoparticles, which may rationalize the high reforming activity. The improved stability on the Ni/m‐ZrO2@Al2O3 catalyst was mainly related to the alleviated carbon deposition endowed by enriched surface basicity and strengthened metal‐support interactions. This article is protected by copyright. All rights reserved.</section>

STUDIES ON STEAM REFORMING OF METHANE OVER Ni/ZrO2 CATALYST

Nickel‐Catalyzed Dry Reforming of Methane Via Modulating the Zirconia Shapes

Influences Of Reaction Conditions On Steam Reforming Of Methane Over Ni/Zro2 Catalyst.

Reforming of methane and coalbed methane over nanocomposite Ni/ZrO2 catalyst

Steam Reforming of Methane over Ni Catalysts Prepared from Hydrotalcite-Type Precursors: Catalytic Activity and Reaction Kinetics

Catalytic performance of Ni catalysts for steam reforming of methane at high space velocity

Reforming Of Methane And Coalbed Methane Over Nanocomposite Nni/Zro2.

Stable Ni/ZrO2 catalyst for carbon dioxide reforming of methane

Study on CO2 reforming of methane to syngas over Al 2O3-ZrO2 supported Ni catalysts prepared via a direct sol-gel process

Methane reforming over Ni/Ce-ZrO2 catalysts: effect of nickel content

Carbon Dioxide Reforming of Methane Over Nanocomposite Ni/ZrO 2 Catalysts

Steam reforming of ethanol for hydrogen production over NiO/ZnO/ZrO2 catalysts

Catalytic Performance and Characterization of Ni–CaO–ZrO2 Catalysts for Dry Reforming of Methane

Low-temperature CO2 Reforming of Methane on Zr-promoted Ni/SiO2 Catalyst

Highly Active and Stable Ni/ZrO2 Catalyst for Syngas Production by CO2 Reforming of Methane

A nanoscale Ni/ ZrO 2 catalyst coated with Al 2 O 3 for carbon dioxide reforming of methane

Carbon Dioxide Reforming of Methane over Ni-based Catalyst

The Influence of Reduction Temperature on the Performance of ZrOx/Ni-MnOx/SiO2 Catalyst for Low-Temperature CO2 Reforming of Methane

Combined Catalytic Partial Oxidation and CO2 Reforming of Methane over ZrO2-modified Ni/SiO2 Catalysts Using Fluidized-Bed Reactor

Synthesis of nickel catalysts supported on Zr-doped ordered mesoporous Al2O3 and their catalytic performance for low-temperature CO2 reforming of CH4

Methane Autothermal Reforming with CO2 and O2 to Synthesis Gas at the Boundary Between Ni and ZrO2