Abstract:This work aims to improve the oxidation resistance of multi-arc ion plated NiCoCrAlY coatings and explore the effect of electroless Pt plating on the oxidation behavior of NiCoCrAlY coating at high temperature.A 0.5μm-thick Pt film was prepared on the multi-arc ion plated NiCoCrAlY coating by electroless plating combined with following vacuum annealing treatment.The high temperature oxidation performance of the coatings before and after modification by electroless Pt plating were tested by isothermal temperature oxidation and cyclic oxidation tests at 1 050℃in air,and the phase composition,morphology and element distribution of the coatings were analyzed by means of scanning electron microscopy （SEM）,X-ray diffraction （XRD） and electron probe micro-analyzer （EPMA）.The results revealed that the NiCoCrAlY coating exhibited a higher oxidation rate in the process of isothermal oxidation for 20 h,and its oxidation weight gain,average thickness of oxide film and oxidation rate constant were 0.78 mg/cm~2,2.31μm and 6.32×10 -12 g~2/（cm~4·s）,respectively.In contrast,after being modified by electroless Pt plating,the isothermal oxidation rate of the NiCoCrAlY coating was reduced significantly,and its oxidation weight gain,average thickness of oxide film and oxidation rate constant were decreased to 0.47 mg/cm~2,0.83μm and2.16×10 -12 g~2/（cm~4·s）,respectively.The modification of electroless Pt plating also effectively improved the cyclic oxidation performance of the NiCoCrAlY coating.After cyclic oxidation for 300 times,the oxidation weight gain was decreased from1.52 mg/cm~2 to 1.05 mg/cm~2,the average thickness of oxide film was reduced from about 5.77μm to 3.62μm and the oxidation rate constant was decreased from 1.93×10 -12 g~2/（cm~4·s） to 9.86×10 -13 g~2/（cm~4·s）.The phase composition of the oxide film formed on the NiCoCrAlY coatings before and after modification by electroless Pt plating during the isothermal temperature oxidation and cyclic oxidation were α-Al 2 O 3 .However,the α-Al 2 O 3 film formed on the NiCoCrAlY coating under the two oxidation conditions has obvious fluctuations,and also grown into the coating in local areas.It can also be observed that local peeling of the oxide film occurred in the later stage of cyclic oxidation.After modification by electroless Pt plating,the α-Al 2 O 3 film formed on the NiCoCrAlY coating was obviously thinner,with higher compactness and flatness,without cracking and peeling.At the same time,the growth of oxide film into the coating was effectively inhibited.It can be seen that the modification by electroless Pt plating can further improve the high temperature oxidation resistance of the multi-arc ion plated NiCoCrAlY coating.This is mainly due to the following two reasons:（1） The gaps in the NiCoCrAlY coating were effectively filled by electroless Pt plating,which improved the compactness of the coating and inhibited the growth of α-Al 2 O 3 film into the coating.（2） High affinity between Pt element and Al element promoted the rapid diffusion of Al element in the coating to the surface,resulting in the rapid formation of thinner and denser α-Al 2 O 3 film.In short,electroless Pt plating is conducive to further expand the application of multi-arc ion plated NiCoCrAlY coating in the field of high temperature protection.

Oxidation Property and Failure Mechanism of A Single Phase Ptal2 Coating

Influence factors of high temperature oxidation for Pt-modified-aluminide bond coatings

Different Growth Mechanisms of Alumina on the Surface of NiPtAl and MCrAlY Bondcoatings in EB-PVD TBC System

TGO stress growth for Pt-modified aluminide bond coats during high temperature oxidation

Oxidation Behavior and Oxide Transformation of a Pt-Modified Aluminide Coating at Moderate High Temperature

Microstructure Analysis of Initial Alumina of Pt-Modified Aluminide Coatings on Ni-Based Alloy

High-temperature performance of Pt-modified Ni-20Co-28Cr-10Al-0.5Y coating: Formation mechanism of Pt-rich overlayer and its effect on thermally grown oxide failure

On the Thermal Shock Resistance and Failure Mechanism of the Pt-Modified Aluminide Bond Coating

Hot Corrosion and Cyclic Oxidation Performance of a Ptal2-Dispersed (ni,pt)al Coating Prepared by Low-Activity High-Temperature Aluminizing

Preparation and Enhanced Hot Corrosion Resistance of a Zr-Doped PtAl2+(Ni, Pt)Al Dual-Phase Coating

Effect of Pt on Stress Rupture Properties of Pt-Modified Nickel Aluminide Coatings at 1100 °C

High-temperature Corrosion Behaviour of Pt-modified Aluminide Coating with Solid NaCl Deposit in O2 + 10 Vol% H2O and the Influence of Pre-Oxidation Treatment

Impact of Pt/Al ratios on the cyclic oxidation and TCP precipitation of β-(Ni, Pt)Al coated superalloy at 1150 °C

High-temperature Performance of (ni,pt)al Coatings on Second-Generation Ni-base Single-Crystal Superalloy at 1100 °C: Effect of Excess S Impurities

Cyclic oxidation behavior of Pt modified NiCoCrAlYHfZr + AlNiY coating on a Ni-based single crystal superalloy

Enhancing long-term cyclic oxidation performance of a dual-phase PtAl coatings at 1200 °C by Ru modification

Oxidation Performance and Interdiffusion Behavior of a Pt-Modified Aluminide Coating with Pre-deposition of Ni

Cyclic oxidation and rumpling behaviour of single phase β-(Ni,Pt)Al coatings with different thickness of initial Pt plating

Effect of Electroless Pt Plating on High Temperature Oxidation Behavior of Multi-arc Ion Plated NiCoCrAlY Coating

High-Temperature Corrosion Behaviour of Pt-Modified Aluminide Coating under the Effect of Nacl Plus Water Vapour and the Influence of Pre-Oxidation Treatment

A novel approach to coating for improving the comprehensive high-temperature service performance of TiAl alloys