Abstract:Microstructure degradation caused by interdiffusion between coating and superalloy is an important factor affecting the performance of thermal barrier coatings. Tuning the interdiffusion microstructure of PtAl Coatings/Superalloys interface is the key to preparing high performance thermal barrier coatings. In this paper, two β-(Ni, Pt)Al coatings with different compositions and thicknesses were first deposited on the same nickel-based single-crystal superalloy by regulating the aluminizing time. After the isothermal oxidation at 1100 °C, a typical two-layer structure forms in the two different coating/superalloy specimens but with different interdiffusion microstructures. It was found that a noticeable secondary reaction zone (SRZ) with topologically close-packed (TCP) precipitates develop in the specimen with 6 h aluminizing after oxidation for 36 h and its thickness continuously increase. By contrast, no SRZ forms in the specimen with 4.5 h aluminizing after oxidation for even 100 h, but only the microstructure transformation of the interdiffusion zone (IDZ) occurred. That is mainly due to the existence of an incomplete transformed sublayer in the as-prepared specimen with a short aluminizing time, which may affect the subsequent interdiffusion of Al, Ni, and refractory elements. It is highly expected that regulating the aluminizing time is an effective strategy to tune the interdiffusion structure between coating and substrate, which should be helpful for designing the coating/substrate system with better performance.

Enhancing long-term cyclic oxidation performance of a dual-phase PtAl coatings at 1200 °C by Ru modification

Effects of coating growth mode on the oxidation behavior of a hybrid Pt/Ru-modified aluminide coating at 1200 °C

Cyclic oxidation-induced deleterious effects of Ru on the surface rumpling of a Pt-modified aluminide coating

Influence factors of high temperature oxidation for Pt-modified-aluminide bond coatings

Cyclic oxidation behavior of Pt modified NiCoCrAlYHfZr + AlNiY coating on a Ni-based single crystal superalloy

High-temperature performance of Pt-modified Ni-20Co-28Cr-10Al-0.5Y coating: Formation mechanism of Pt-rich overlayer and its effect on thermally grown oxide failure

Investigation on the microstructural evolution and oxidation resistance of Ru-doped NiAlHf coatings at 1200 °C

Effect of Pt on Stress Rupture Properties of Pt-Modified Nickel Aluminide Coatings at 1100 °C

A novel single-phase γ′ nanocrystalline coating with high resistance to oxidation and scale rumpling yet mitigated interdiffusion with the alloy substrate

Preparation and Enhanced Isothermal Oxidation Resistance of a Low Diffusivity NiRePtAl Single-Phase Coating

Impact of Pt/Al ratios on the cyclic oxidation and TCP precipitation of β-(Ni, Pt)Al coated superalloy at 1150 °C

The cyclic oxidation behavior of a Pt modified γ' nanocrystalline coating at 1150 °C

Pt-modification on the thermal cycling behavior of NiCoCrAlYTa coating: a case study

Tensile crack inhibition of a PtReAl coated Ni 3 Al-based single crystal superalloy after long-term oxidation

Combined effect of Ru on the oxidation behavior and microstructure stability of a single crystal superalloy

Cyclic Oxidation Behaviour of Pt-doped Aluminide Coating on DZ125 Containing Hf

The potential application of Ru in aluminide coatings with reduced Al contents: A combined experimental and theoretical study

Microstructure Analysis of Initial Alumina of Pt-Modified Aluminide Coatings on Ni-Based Alloy

Influence of Pt on oxidation behavior of CoNiCrAlY alloy

Tuning the secondary reaction zone between PtAl coating and nickel based single crystal superalloy during high-temperature oxidation through regulating aluminizing time

A novel approach to coating for improving the comprehensive high-temperature service performance of TiAl alloys