Abstract:Pt-modified aluminide coating has attracted great attention due to its advantage of the integrated property in resisting both high temperature oxidation and hot corrosion. By the presence of Pt, the spallation trend of the grown oxide scale and the detrimental effect of S can be restrained at a very low level. Besides, Pt could promote alpha-Al2O3 formation and stabilize beta-NiAl phase. Thus Pt-modified aluminide (Pt-Al) coating has been widely used in some crucial applications requiring reliability and extended service life. There are mainly PtAl2, beta-(Ni, Pt) Al and gamma/gamma'-NiPtAl phases existing inside Pt-Al coating. In this work, a single phase PtAl2 coating was prepared on a Ni-based K38G superalloy through pulse-electroplating of Pt and pack aluminization under stepped heating mode. At 1100 degrees C, the isothermal oxidation behavior of the single phase PtAl2 coating was evaluated by thermogravimetric analysis (TGA). Cyclic oxidation test of the PtAl2 coating was performed within a vertical muffle furnace at the same temperature. The results indicate that the singular PtAl2 coating possesses quite good isothermal oxidation resistance. However, its resistance against cyclic oxidation is very poor. The cyclic stress induced by repeated heating and cooling has caused visible detachment of PtAl2 coating layer, and the spallation of PtAl2 in further would lead to a premature failure of the whole coating system. Partial spallation of PtAl2 layer, including undesirable consumption of Al inside beta-NiAl nearby the spallation acts the main reason responsible for the final failure. Accordingly, it is not appropriate to apply single phase PtAl2 coating in the high temperature services involving stress and load. The degradation mechanism of the singular PtAl2 coating is investigated by discussing the stress generated from cyclic heating and cooling.

The cyclic oxidation behavior of a Pt modified γ' nanocrystalline coating at 1150 °C

A novel single-phase γ′ nanocrystalline coating with high resistance to oxidation and scale rumpling yet mitigated interdiffusion with the alloy substrate

TGO stress growth for Pt-modified aluminide bond coats during high temperature oxidation

Cyclic oxidation and rumpling behaviour of single phase β-(Ni,Pt)Al coatings with different thickness of initial Pt plating

Understanding of failure mechanisms of the oxide scales formed on nanocrystalline coatings with different Al content during cyclic oxidation

Oxidation Behavior and Oxide Transformation of a Pt-Modified Aluminide Coating at Moderate High Temperature

Cyclic oxidation behavior of Pt modified NiCoCrAlYHfZr + AlNiY coating on a Ni-based single crystal superalloy

Impact of Pt/Al ratios on the cyclic oxidation and TCP precipitation of β-(Ni, Pt)Al coated superalloy at 1150 °C

High-temperature performance of Pt-modified Ni-20Co-28Cr-10Al-0.5Y coating: Formation mechanism of Pt-rich overlayer and its effect on thermally grown oxide failure

Effect of γ′ Phase Elements on Oxidation Behavior of Nanocrystalline Coatings at 1050 °C

Pt-modification on the thermal cycling behavior of NiCoCrAlYTa coating: a case study

The influence of Cr on the oxidation behavior of a sputtered Pt+γ' phase-equilibrium coating at 1150 °C

Modification of NiCoCrAlY with Pt: Part I. Effect of Pt Depositing Location and Cyclic Oxidation Performance

Oxidation Property and Failure Mechanism of A Single Phase Ptal2 Coating

Oxidation characteristics of gamma-TiAl-8Nb coated with a CrAlYN/CrN nanoscale multilayer coating

Enhancing long-term cyclic oxidation performance of a dual-phase PtAl coatings at 1200 °C by Ru modification

Breakaway Oxidation of a Low-Al Content Nanocrystalline Coating at 1000 °C

Microstructure Analysis of Initial Alumina of Pt-Modified Aluminide Coatings on Ni-Based Alloy

Effect of Al and Cr on the oxidation behavior of nanocrystalline coatings at 1050 °C

Preparation, Mechanical Properties and Cyclic Oxidation Behavior of the Nanostructured NiCrCoAlY-TiB2 Coating

Oxidation Behavior of Graded NiCrAlYRe Coatings at 900, 1000 and 1100 °C