High-temperature performance of Pt-modified Ni-20Co-28Cr-10Al-0.5Y coating: Formation mechanism of Pt-rich overlayer and its effect on thermally grown oxide failure
Chuntang Yu,Wanqi Pu,Shuai Li,Zebin Bao,Renju Cheng,Chengyang Jiang,Zhengliang Liu,Wei Zhang,Lei Zhang,Suibo Zhao,Hanqing Xie,Shenglong Zhu,Fuhui Wang
DOI: https://doi.org/10.1016/j.surfcoat.2023.129422
IF: 4.865
2023-03-19
Surface and Coatings Technology
Abstract:A Pt-modified NiCoCrAlY coating was prepared on N5 via arc ion plating (AIP), Pt-electroplating, and subsequent vacuum annealing treatments. To perform a comparison between the properties of the modified and normal NiCoCrAlY coatings, the isothermal oxidation performances of the Pt-free and Pt-modified NiCoCrAlY coatings were evaluated at 1100 °C in static air. The results indicate that the Pt-rich overlayer on the Pt-modified NiCoCrAlY coatings exhibited superior oxidation resistance, and the adherent, thinner scale of α-Al 2 O 3 inhibited the formation of detrimental (Ni, Co)(Cr, Al) 2 O 4 spinel oxide. Furthermore, the addition of Pt effectively delayed the Al 2 O 3 oxide phase transformation from θ to α in the early stage and markedly decreased the level of residual stress. The mechanism of forming the Pt-rich overlayer and its effect on thermally grown oxide (TGO) failure during high-temperature oxidation are discussed in detail, and the effect of Pt on improving the TGO growth, stress evolution, and spallation resistance are highlighted.
physics, applied,materials science, coatings & films