Effect of Sc on the water vapor oxidation behavior of FeCrAl alloys at 1000 °C
Shiting Yang,Hongliang Sun,Xili Liu,Weiwen Yan,Rui Liu,Xiaosong Jiang
DOI: https://doi.org/10.1002/adem.202400125
IF: 3.6
2024-06-27
Advanced Engineering Materials
Abstract:This study analyzes the oxidation behavior of FeCrAl‐(0.0, 0.5, 1.0, 2.0, and 4.0) wt.% Sc alloys prepared through vacuum hot‐press sintering in a water vapor environment. Sc diffuses via short‐circuit diffusion from the oxide scale/alloy interface to the oxide scale surface. Subsequently, Sc is segregated at the aluminum oxide scale interface, preventing Al ions from diffusing outwards to combine with the oxygen in the water vapor and reducing the growth rate of the oxide scale. Compared to a pure oxygen atmosphere, the water vapor atmosphere affects the adhesion of the oxide scale, shedding the oxide scale and leading to secondary oxidation. Sc doping transforms the oxide scale from a state of easily curved, poorly bonded, and full voids into a flat, bonded, dense, and protective scale. This improves the bonding and anti‐curling abilities of the oxide scale. A dopant content of 0.5 wt.% Sc is low and has a minor effect on the oxidation resistance of FeCrAl alloys. Samples containing 2.0 and 4.0 wt.% Sc are excessively doped, causing considerable internal oxidation. In this experiment, 1.0 wt.% Sc doping was found to be the most appropriate, demonstrating a low mass gain of 2.59 ± 0.12 mg/cm2 and a slow oxidation rate (rate constant Kp = 0.7131 mg/cm2 ·hn). Sc‐doped FeCrAl alloys used for improving high‐temperature oxidation resistance should preferably contain less than 2.0 wt.% Sc, with ∽1.0 wt.% being more appropriate. This article is protected by copyright. All rights reserved.
materials science, multidisciplinary