Abstract:Yttria-stabilized zirconia (YSZ) thin films on polycrystalline substrates were grown by cold-wall aerosol-assisted metallorganic chemical vapor deposition (MOCVD) at the temperatures of 673-1233 K using metal beta-diketonate chelates as precursors. Thin uniform films with amorphous structure were obtained below 673 K; when the deposition temperature increases to 773-1023 K, YSZ films appear to be a mixture of cubic and monoclinic phases; single cubic YSZ phase can be obtained at deposition temperature above 1023 K. The Y/Zr atom ratio estimated from the corresponding X-ray photoelectron spectroscopy peaks is less than the feed ratio, which can be interpreted by different transfer resistance of Y and Zr intermediates diffusing to the substrate surface. The films obtained at 673-1023 K possess a layer structure originated from low mobility of the absorbed species. Along with the increase of the deposition temperature, the grains become mature and larger, and then unite with each other to form a continuous columnar film. Mass transport dominates the growth process within lower temperatures, and homogeneous reaction will interrupt the growth at increasingly high temperatures. Growth rate expression with respect to temperature, pressure, gas flow rate, and metal concentration of precursor solutions was deduced assuming deposition of mass-transport limited mechanism, which is consistent with the experimental results. (c) 2005 The Electrochemical Society. All rights reserved.

Preparation of t-ZrO2 by a sol–gel process with carbon as a phase transformation promoter

Formation and Rate Processes of Y2o3 Stabilized Zro2 Thin Films from Zr(Dpm)(4) and Y(Dpm)(3) by Cold-Wall Aerosol-Assisted Mocvd

Preparation of Zirconia Powders by Sol-gel Process

A General Propylene Epoxide-assisted Sol-Gel Route for the Synthesis of ZrO2-SnO2 Composite Sols

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Preparation and Thermochromic Properties of Sol-Gel-derived Zr-doped VO 2 Films

Preparation of Li-doped ZrO2 Porous Monoliths via Sol-Gel Process Accompanied by Phase Separation

Synthesis of Monolithic Zirconia with Macroporous Bicontinuous Structure Via Epoxide-Driven Sol–gel Process Accompanied by Phase Separation

Preparation and characterization of ZnO-B2O3-SO2 by sol-gel method

Formation and transformation of ZnTiO3 prepared by sol–gel process

Crystallization of t-ZrO2 in zirconia powder prepared by sol-gel process

Preparation and Characterization of ZnO-B2O3-SiO2 by Sol-Gel Method

The Preparation,Stability of Zirconium Sol and Characteristics of ZrO_2 Powder

Preparation of Macroporous Zirconia Monoliths via Sol-Gel Process Accompanied by Phase Separation

The Self-Catalytic Role Of Zirconium N-Propoxide In Sol-Gel Syntheses Of Zro2/Y2o3-Ceo2 Compound Powders

The Self-Catalytic Role of Zirconium N-Propoxide in Sol-Gel Syntheses of ZrO<sub>2</sub>/Y<sub>2</sub>O<sub>3</sub>-CeO<sub>2</sub> Compound Powders

Preparation and CO 2 Capture Properties of Nanocrystalline Li 2 ZrO 3 Via an Epoxide-Mediated Sol–gel Process

Scalable Preparation of Hollow ZrO2 Microspheres Through a Liquid-Liquid Phase Reunion Assisted Sol-Gel Method

Stabilization of Cubic Zirconia by Carbon Nanotubes

Phase Composition Controllable Preparation of Zirconia Nanocrystals Via Solvothermal Method

Preparation of macroporous zirconia monoliths from ionic precursors via an epoxide-mediated sol-gel process accompanied by phase separation