Hot Deformation Induced Defects and Performance Enhancement in FeSb2 Thermoelectric Materials

Yongzheng Wang,Chenguang Fu,Tiejun Zhu,Lipeng Hu,Guangyu Jiang,Guanghui Zhao,Dexuan Huo,Xinbing Zhao
DOI: https://doi.org/10.1063/1.4831668
IF: 2.877
2013-01-01
Journal of Applied Physics
Abstract:The effect of hot deformation induced defects and texture on thermoelectric properties of FeSb2 bulk crystals has been investigated. The transport properties of the samples along both parallel and perpendicular direction of pressing were measured from 3 K to 300 K. The results showed that thermal conductivity of the deformed samples was significantly reduced. After twice deformation, the thermal conductivity of the sample along the perpendicular direction of pressing was decreased to 4 W/mK, which was only one third of that before deformation. Transmission electron microscopy observation revealed the presence of high density of lattice defects in the deformed samples. The lattice thermal conductivity was analyzed using the Debye-Callaway approximation, and the results showed that the deformation induced lattice imperfections play an important role in enhancing phonon scattering. In addition, both the electrical resistivity and Seebeck coefficient exhibited a weak anisotropy in the deformed samples. The figure of merit ZT of the bulk FeSb2 was significantly improved from 0.010 to 0.021 after deformation.
What problem does this paper attempt to address?