Abstract:Bi2Te3-based materials are dominating thermoelectrics for almost all of the room-temperature applications. To meet the future demands, both their thermoelectric (TE) and mechanical properties need to be further improved, which are the requisite for efficient TE modules applied in areas such as reliable micro-cooling. The conventional zone melting (ZM) and powder metallurgy (PM) methods fall short in preparing Bi2Te3-based alloys, which have both a highly textured structure for high TE properties and a fine-grained microstructure for high mechanical properties. Herein, a mechanical exfoliation combined with spark plasma sintering (ME-SPS) method is developed to prepare Bi0.5Sb1.5Te3 with highly improved mechanical properties (correlated mainly to the dislocation networks), as well as significantly improved thermoelectric properties (correlated mainly to the texture structure). In the method, both the dislocation density and the orientation factor (F) can be tuned by the sintering pressure. At a sintering pressure of 20 MPa, an exceptional F of up to 0.8 is retained, leading to an excellent power factor of 4.8 mW m-1 K-2 that is much higher than that of the PM polycrystalline. Meanwhile, the method can readily induce high-density dislocations (up to ∼1010 cm-2), improving the mechanical properties and reducing the lattice thermal conductivity as compared to the ZM ingot. In the exfoliated and then sintered (20 MPa) sample, the figure-of-merit ZT = 1.2 (at 350 K), which has increased by about ∼20%, and the compressive strength has also increased by ∼20%, compared to those of the ZM ingot, respectively. These results demonstrate that the ME-SPS method is highly effective in preparing high-performance Bi2Te3-based alloys, which are critical for TE modules in commercial applications at near-room temperature.

Microstructure and thermoelectric properties of porous Bi 2 Te 2.85 Se 0.15 bulk materials fabricated by semisolid powder processing

Enhanced thermoelectric performance of n -type PbTe bulk materials fabricated by semisolid powder processing

Ultrasonic-assisted Hot Pressing of Bi2Te3-based Thermoelectric Materials

Introduction of Porous Structure: A Feasible and Promising Method for Improving Thermoelectric Performance of Bi2Te3 Based Bulks

Improved Thermoelectric Properties of Bi2Te3−xSexalloys by Melt Spinning and Resistance Pressing Sintering

Porosity Induced Thermoelectric Performance Optimization for Antimony Telluride

High thermoelectric and mechanical performance in strong-textured n-type Bi2Te2.7Se0.3 by temperature gradient method

Effect of spark plasma sintering temperature on thermoelectric properties of Bi 2 S 3 polycrystal

Porous bismuth antimony telluride alloys with excellent thermoelectric and mechanical properties

Enhanced Thermoelectric and Mechanical Performances in Sintered Bi0.48Sb1.52Te3-AgSbSe2 Composite.

Enhancing thermoelectric properties of p-type (Bi,Sb)2Te3 via porous structures

Mechanically Robust BiSbTe Alloys with Superior Thermoelectric Performance: A Case Study of Stable Hierarchical Nanostructured Thermoelectric Materials

Regulation of Dynamic Recrystallization in P-Type Bi2Te3-Based Compounds Leads to High Thermoelectric Performance and Robust Mechanical Properties

Enhanced thermoelectric properties of bismuth sulfide polycrystals prepared by mechanical alloying and spark plasma sintering

Enhanced Thermoelectric and Mechanical Performances in Sintered Bi 0.48 Sb 1.52 Te 3 –AgSbSe 2 Composite

Enhancing the Thermoelectric and Mechanical Properties of Bi<sub>0.5</sub>Sb<sub>1.5</sub>Te<sub>3</sub> Modulated by the Texture and Dense Dislocation Networks

Cold-Sintered Bi 2 Te 3 -Based Materials for Engineering Nanograined Thermoelectrics

Enhanced thermoelectric performance of hot-press Bi-doped n-type polycrystalline PbS

Preparation and Thermoelectric Properties of Nanoporous Bi 2 Te 3 -Based Alloys

Enhancing the Thermoelectric and Mechanical Properties of Bi 0.5 Sb 1.5 Te 3 Modulated by the Texture and Dense Dislocation Networks

Improved thermoelectric performance in p-type Bi0.48Sb1.52Te3 bulk material by adding MnSb2Se4 *