Abstract:The 7075 aluminium matrix composite reinforced with nano-sized Si C particles was fabricated by ultrasonic assisted semisolid stirring method. The compression mechanical behaviour of the fabricated composite in semisolid state was investigated. The results show that the microstructure of the composite before semisolid compression consists of fine and spheroidal solid grains surrounded by liquid phase.Semisolid compression led to a nonuniform plastic deformation of solid grains. A slight plastic deformation occurred in the locations near the free surface due to the dependence of deformation on liquid flow and flow of liquid incorporating solid grains. However, obvious plastic deformation occurred in the central location and location contacting to die due to the contribution of plastic deformation of solid grains.The true stress–strain curve of the sample compressed at 500 °C consists of rapid increase of true stress and steady stage. However, rapid increase of true stress and decrease of true stress and steady stage are involved in the true stress–strain curves of the samples compressed at 550, 560, 570, 580 and 590 °C.The true stress–strain curve at 600 °C is similar to that at 500 °C. Apparent viscosity decreases with an increase of shear rate, indicating a shear thinning occurrence. When soaking time increases from 5 min to 15 min, the peak stress and steady stress decrease significantly. A further increase of the soaking time led to a slight change. Peak stress and steady stress increase with increasing volume fraction of Si C particles. A sudden increase or decrease of compression velocity led to a significant increase or decrease of the steady stress. The destruction of the samples compressed at solid state temperature mainly depends on cracks parallel to compression direction. However, the destruction forms of the samples compressed at semisolid temperatures consist of cracks parallel to compression direction and partial collapse. Increasing soaking time led to an obvious change of the destruction forms. Compression velocity affects slightly the macro appearance of the sample compressed at semisolid temperatures.

Performance and Phase Behavior of Quartz-Aluminum Matrix Composites

Characterization of Aluminium Matrix Compositesreinforced by Al–Cu–Fe-Cr Quasicrystalline Particles

High Temperature Mechanical Property of Al2O3 Coated Quartz-Fiber Reinforced Methyl Silicon Resin Composites

Preparation and properties of Al2O3/Al-2(1-0.2)Mg0.2Ti(1+0.2)O5 matrix ceramic composite

Influence of Reinforcement with Multimodal Distribution on Thermophysical Properties and Fracture Behavior in Al-Si/SiC Composites Infiltrated under Super-Gravity Field

High-temperature properties of Al 2 O 3 /SiO 2 composites

Ambient and Elevated Temperature Mechanical Properties of Hot-Pressed Fused Silica Matrix Composite

Mechanical properties of low-temperature sintered Al2O3/3Y-TZP composites

Enhanced Mechanical Properties of SiC/Al Composites at Cryogenic Temperatures

FABRICATION AND PROPERTIES OF CALCIUM-HEXALUMINATE/MAGNESIUM-ALUMINIUM SPINEL COMPOSITES

Compression Testing of a SiCw/Al Composite at Temperatures Close to and above the Solidus of the Matrix Alloy

Effect of LaMgAl11O19 Addition and Temperature on the Mechanical Properties of Al2O3-based Ceramics

High temperature compression behavior of Al2O3 particle reinforced 6061aluminum alloy composite

Compression Mechanical Behaviour of 7075 Aluminium Matrix Composite Reinforced with Nano-sized SiC Particles in Semisolid State

Hot strength and microstructure of β-sialon-Al2O3-SiC composites

Preparation and properties of MgAl 2O 4-CaAl 12O 19 high temperature composite

Microstructure and mechanical properties of the α-SiAlON/α-SiC composites: Effects of heat treatment

Thermal expansion and dimensional stability of Al–Si matrix composite reinforced with high content SiC

Mechanical and thermal properties of Al 2O 3-ZrO 2 composite ceramics at cryogenic temperatures

Microstructural Changes of SiCw/6061Al Composite During Compression at Temperatures below and above the Solidus of the Matrix Alloy

Phase transition and mechanical properties of al-based composites reinforced by Al72Ni12Co16 decagonal quasicrystalline particles