Abstract:The 7075 aluminium matrix composite reinforced with nano-sized Si C particles was fabricated by ultrasonic assisted semisolid stirring method. The compression mechanical behaviour of the fabricated composite in semisolid state was investigated. The results show that the microstructure of the composite before semisolid compression consists of fine and spheroidal solid grains surrounded by liquid phase.Semisolid compression led to a nonuniform plastic deformation of solid grains. A slight plastic deformation occurred in the locations near the free surface due to the dependence of deformation on liquid flow and flow of liquid incorporating solid grains. However, obvious plastic deformation occurred in the central location and location contacting to die due to the contribution of plastic deformation of solid grains.The true stress–strain curve of the sample compressed at 500 °C consists of rapid increase of true stress and steady stage. However, rapid increase of true stress and decrease of true stress and steady stage are involved in the true stress–strain curves of the samples compressed at 550, 560, 570, 580 and 590 °C.The true stress–strain curve at 600 °C is similar to that at 500 °C. Apparent viscosity decreases with an increase of shear rate, indicating a shear thinning occurrence. When soaking time increases from 5 min to 15 min, the peak stress and steady stress decrease significantly. A further increase of the soaking time led to a slight change. Peak stress and steady stress increase with increasing volume fraction of Si C particles. A sudden increase or decrease of compression velocity led to a significant increase or decrease of the steady stress. The destruction of the samples compressed at solid state temperature mainly depends on cracks parallel to compression direction. However, the destruction forms of the samples compressed at semisolid temperatures consist of cracks parallel to compression direction and partial collapse. Increasing soaking time led to an obvious change of the destruction forms. Compression velocity affects slightly the macro appearance of the sample compressed at semisolid temperatures.

Compression Testing of a SiCw/Al Composite at Temperatures Close to and above the Solidus of the Matrix Alloy

Forming process of hot-extruded SiCw/6061AI composites(I)

Microstructural Changes of SiCw/6061Al Composite During Compression at Temperatures below and above the Solidus of the Matrix Alloy

Microstructure and properties of SiCw/6061 aluminium alloy composites after compression at temperatures around solidus of matrix

Investigation of Compression of Sicw/6061al Composites Around the Solidus of the Matrix Alloy

Deformability of a SiCw/6061Al composite during high strain rate compression at elevated temperatures

Hot Deformation Behavior of SiCw/AZ91 Magnesium Matrix Composite in Compression

Compressive deformation behavior of α-Si3N 4w/4032 Al composite at elevated temperatures

Hot Deformation Behavior and Mechanisms of SiC Particle Reinforced Al-Zn-Mg-Cu Alloy Matrix Composites

Compression Mechanical Behaviour of 7075 Aluminium Matrix Composite Reinforced with Nano-sized SiC Particles in Semisolid State

Compressive Deformation Behavior of the SiCw/AZ91 Composite at Elevated Temperatures

Investigation of high-temperature deformation behavior of a SiC whisker reinforced 6061 aluminium composite

High temperature compression behavior of Al2O3 particle reinforced 6061aluminum alloy composite

Effects of Hot Compression on Microstructure of SiC_p/Al Composite with High Volume Fraction

Compressive Stress-Strain Response of Directionally Aligned Sicw/Al Composite

Deformation and damage mechanisms of SiC/Al matrix composite under high compressive stain

HOT DEFORMATION BEHAVIOR OF SiCw/AZ91 MAGNESIUM MATRIX COMPOSITE AND AZ91 ALLOY

Age-hardening Behavior of a SiCw/Al-Li-Cu-Mg-Zr Composite

Compressive Behavior of Extruded SiCw/AZ91 at Temperatures Close to and above the Solidus of the Matrix Alloy

Compressive Deformation Of A -Si3n4 W/4032ai Composite At Temperatures Around The Solidus Of The Matrix Alloy

Compressive deformation behavior of alpha-Si(3)N(4)w/4032 Al composite at elevated temperatures