Abstract:In this study, the continuous alumina fibers reinforced alumina matrix (Al2O3/Al2O3) composites were fabricated through sol–gel method at a sintering temperature range of 900–1400 °C, and their mechanical properties were analyzed separately. To explore the effects of sintering temperature on mechanical properties of composites, the high temperature properties of fibers and matrix were studied in a comprehensive manner. Our results suggested that the composites fabricated at different temperatures exhibited two different fracture features (ductile fracture and brittle fracture). Besides, the 1100 °C fabricated composites possessed the highest flexural strength of nearly 150 MPa. Al2O3 fibers displayed excellent thermal stability, and did not undergo phase transition during the preparation process. However, the grain size of fibers increased dramatically at a sintering temperature of 1200 °C, which led to a significant decrease in the mechanical properties. In the meantime, the surface morphology of fibers became very uneven because of grain coarsening. Due to the phase transition from γ-Al2O3 to α-Al2O3 at 1200 °C, the elastic modulus and microhardness of matrix increased significantly. The higher sintering temperature not only intensified the matrix but also strengthened the interface bonding, thus making the composites prone to brittle fracture. In conclusion, the optimal temperature of composites preparation should be lower than 1200 °C.

High Temperature Mechanical Property of Al2O3 Coated Quartz-Fiber Reinforced Methyl Silicon Resin Composites

Liquid-phase deposition of Al2O3 coating on quartz fiber for enhanced strength at elevated temperature

High-temperature properties of Al 2 O 3 /SiO 2 composites

The Influence of Pbo Coating on Room Temperature Mechanic Properties of Heat-Treated Quartz Fiber-Reinforced Methyl Silicon Resin Composites I. Flexural Properties

Effect of LaMgAl11O19 Addition and Temperature on the Mechanical Properties of Al2O3-based Ceramics

Effect of heat‐treatment on the microstructure and room‐temperature mechanical properties of alumina–silica fiber

Performance and Phase Behavior of Quartz-Aluminum Matrix Composites

Effects of sintering temperature on mechanical properties of alumina fiber reinforced alumina matrix composites

Synthesis of high-temperature resistance hybrid silicon resin and evaluation of its composite material's high-temperature mechanical property

Preparation and Characterization of Alumina-coated Hollow Quartz Fiber Reinforced Al2O3-SiO2 Aerogel Composite

Ambient and Elevated Temperature Mechanical Properties of Hot-Pressed Fused Silica Matrix Composite

Fabrication and Characterization of Ceramic Coatings with Alumina–silica Sol-Incorporated Α-Alumina Powder Coated on Woven Quartz Fiber Fabrics

Fabrication and high-temperature strength of 2.5D SiO2f /SiO2 composites prepared by a combined vacuum impregnation and sol-gel method

Effects of high-temperature heat treatment on the microstructure and mechanical performance of hybrid Cf-SiCf-(Al2O3p) reinforced geopolymer composites

Improvement of the tensile strength of Al18B4O33w/Al composite at elevated temperatures by change of interfacial state

Fabrication and Thermal Stability of Continuous Carbon Fiber Reinforced Alumina Matrix Composites via Sol–Gel Process

Mechanical properties of the alumina-coated Al18B4O33w/6061Al composites

Effect of thermal exposure on the microstructure and strength of an alumina‐silica ceramic fiber

Thermal Stability, Mechanical Properties and Ceramization Mechanism of Epoxy Resin/Kaolin/Quartz Fiber Ceramifiable Composites

Structure and properties of fine diameter continuous SiC ceramic fiber reinforced Al matrix composites

Effect of TM (tm=fe, Mn, Cr) Alloying on the High Temperature Properties and Strengthening Mechanism of Cf/Al Composites