Interfacial reaction kinetics of (Al63Cu25Fe12) 99Ce1 quasicrystal reinforced 6061 aluminum matrix composites
Juan Wang,Zhong Yang,Liying Wang,Jianping Li
DOI: https://doi.org/10.1016/j.jallcom.2023.170261
IF: 6.2
2023-09-01
Journal of Alloys and Compounds
Abstract:Due to its superior overall characteristics and effective interface wetting, quasicrystal reinforced aluminum matrix composite is regarded as a type of material with significant development potential. The procedure of hot pressing and sintering was used to create a quasicrystal particle reinforced 6061 aluminum matrix composite made of (Al63Cu25Fe12)99Ce1. Investigated in the composite were the element diffusion and the microstructure of the contact between the reinforcement and matrix. The findings demonstrate that mutual diffusion between reinforcement and matrix leads to the formation of the I-phase, Cu9Al4 phase, Al23CuFe4 phase, and ω-phase. Always present in the reinforcement, which has a strong link to the matrix, is the Al13Ce2Cu13 phase. At the same time, the diffusion kinetics of the transition layer between the quasi-crystalline phase and the matrix during the hot pressing process was revealed, and the most suitable thickness of the transition layer was determined to be 4.85 µm, which plays a great role in the improvement of the composite properties. The study of the microstructure and interfacial dynamics of (Al63Cu25Fe12)99Ce1 quasicrystal-reinforced 6061 aluminum matrix composites has laid the foundation for the creation of long-life, high-strength aluminum alloy materials with excellent properties.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering