Abstract:Abstract Textured hexagonal boron nitride (h-BN) matrix composite ceramics were prepared by hot-pressing using different contents of 3Y 2 O 3 −5Al 2 O 3 (molar ratio of 3:5) as the sintering additive. During hot-pressing, the liquid Y 3 Al 5 O 12 (YAG) phase showing good wettability to h-BN grains was in situ formed through the reaction between Y 2 O 3 and Al 2 O 3 , and a coherent relationship between h-BN and YAG was observed with $${\left[ {010} \right]_{{\rm{h}} - {\rm{BN}}}}{\rm{//}}{\left[ {111} \right]_{{\rm{YAG}}}}$$ [ 010 ] h − BN // [ 111 ] YAG and (002) h-BN //(321) YAG . In the YAG liquid phase environment formed during hot-pressing, plate-like h-BN grains were rotated under the uniaxial sintering pressure and preferentially oriented with their basal surfaces perpendicular to the sintering pressure direction, forming textured microstructures with the c -axis of h-BN grains oriented parallel to the sintering pressure direction, which give these composite ceramics anisotropy in their mechanical and thermal properties. The highest texture degree was found in the specimen with 30 wt% YAG, which also possesses the highest anisotropy degree in thermal conductivity. The aggregation of YAG phase was observed in the specimen with 40 wt% YAG, which resulted in the buckling of h-BN plates and significantly reduced the texture degree.

Microstructure and Mechanical Properties of H-Bn/y2sio5 Composites

High-temperature mechanical and thermal properties of h -BN/30vol%Y 2 SiO 5 composite

Preparation And Properties Of Machinable Si2n2o/Bn Composites

Fabrication of High Strength α-SiAlON/BN Composition Ceramics by Hot Pressing

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Microstructure and room/elevated-temperature mechanical properties of hot-pressed h-BN composite ceramics with La2O3-Al2O3-SiO2 addition

Mechanical and wear properties of h-BN/Si3N4 ceramic composites

High-pressure synthesis of Al<sub>2</sub>O<sub>3</sub>-cBN composites: Effect of thermodynamic condition and cBN volume fraction on their microstructure and properties

Effect of Y<sub>2</sub>O<sub>3</sub> on the Sintering, Mechanical and Dielectric Properties of Mullite/h-BN Composites

Microstructure and Mechanical Properties of Y-SiAlON/BaSi2Al2O8 Composite Ceramics

Microstructure of hot-pressed h-BN/Si3N4 ceramic composites with Y2O3–Al2O3 sintering additive

Texture and anisotropy of hot-pressed h-BN matrix composite ceramics with in situ formed YAG

Microstructural Evolution and Mechanical Properties of H-Bn Composite Ceramics with Y 2 O 3 –aln Addition by Liquid-Phase Sintering

Fabrication and properties of Si3N4/BN composite ceramics by pressureless sintering with Yb2O3-Al 2O3-Y2O3 as sintering additives

Anisotropies in structure and properties of hot-press sintered h-BN-MAS composite ceramics: Effects of raw h-BN particle size

Hot-pressed ZrB2–SiC–YSZ Composites with Various Yttria Content: Microstructure and Mechanical Properties

Microstructure and Mechanical Properties of Reactive Hot-Pressed BN-ZrB_2-ZrO_2 Composites

Mechanical and tribological properties of hot-pressed h-BN/Si3N4 ceramic composites

Microstructure, mechanical properties and thermal shock resistance of hot-pressed ZrO2(3Y)-BN composites