Abstract:Y-SiAlON/BaSi2Al2O8 （BAS） composite ceramics were prepared via a hot-press sintering method using the powders of α-Si3N4, Al2O3, AlN, Y2O3 and BAS as raw materials. The effect of BAS content on phase composition, microstructure and mechani- cal properties was investigated. The results reveal that all the materials are fully densified （relative density 〉 99%）, and are composed of the elongated SiAlON grains. The amount of α-SiAlON decreased and the amount of β-SiAlON increased with increasing the BAS content, resulting in a drastic decrease in the hardness and slight decreases in the fracture toughness and elastic module. The Y-SiAlON/10% （in mass）BAS composite ceramics possessed a flexural strength of 775.5 MPa. The pull-out of elongated SiAION grain and the crack deflection both are the main self-toughness mechanisms for Y-SiAlON/BAS composite ceramics.

Microstructure and Mechanical Properties of Y-SiAlON/BaSi2Al2O8 Composite Ceramics