Effect of Y₂O₃ on the Sintering, Mechanical and Dielectric Properties of Mullite/h-BN Composites

Han Jin,Yong Feng Li,Zhong Qi Shi,Hong Yan Xia,Guan Jun Qiao

DOI: https://doi.org/10.4028/www.scientific.net/msf.848.28

2016-01-01

Materials Science Forum

Abstract:Mullite/10 wt. %h-BN composites with 5 wt. % Y2O3 additive were fabricated by pressureless sintering at different temperatures. The densification, phase composition, microstructure, mechanical and dielectric properties of the mullite/h-BN composites were investigated. With the addition of Y2O3, the sintering temperature of the mullite/h-BN composites declined, while the density, mechanical and dielectric properties all increased. The addition of Y2O3 promoted the formation of liquid phase at high temperature, which accelerated the densification. Besides, Y2O3 particles which were located at the grain boundaries inhibited the grain growth of mullite matrix. For the mullite/h-BN composites with Y2O3 additive, the appropriate sintering temperature was about 1600°C. The relative density, flexural strength, fracture toughness and dielectric constant of the Y2O3 doped mullite/h-BN composite sintered at 1600 °C reached 82%, 135 MPa, 2.3 MPa·m1/2 and 4.9, respectively.