Microstructural Evolution of H-BN Matrix Composite Ceramics With Amorphous La2O3-Al2O3-SiO2 Glass Phase During Hot Pressing
Baofu Qiu,Xiaoming Duan,Zhuo Zhang,Chen Zhao,Bo Niu,Peigang He,Delong Cai,Lei Chen,Zhihua Yang,Yujin Wang,Dechang Jia,Yu Zhou
DOI: https://doi.org/10.21203/rs.3.rs-74072/v1
2020-01-01
Abstract:Abstract BN-La 2 O 3 -Al 2 O 3 -SiO 2 composite ceramics were fabricated by hot press sintering using h-BN, La 2 O 3 , Al 2 O 3 and amorphous SiO 2 as the raw materials. The effects of sintering temperature on the microstructural evolution, bulk density, apparent porosity, and mechanical properties of h-BN composite ceramics were investigated. The results indicated that ternary La 2 O 3 -Al 2 O 3 -SiO 2 liquid phase was formed during sintering process, which provided an environment for the growth of h-BN grains. With increasing sintering temperature, the cristobalite phase precipitation and h-BN grain growth occurred at the same time, which had the significant influence on the densification and mechanical properties of h-BN composite ceramics. The best mechanical properties of BN-La 2 O 3 -Al 2 O 3 -SiO 2 composite ceramics were obtained under sintering temperature of 1700 °C, and the elastic modulus, flexural strength, and fracture toughness were 80.5 GPa, 266.4 MPa and 3.25 MPa·m 1/2 , respectively.