Microstructure and Dielectric Properties of Batio3-La2o3-Mgo Ceramic
Wang Yuehui,Zhou Ji,Wang Ting,Shen Jianhong,Cui Xuemin
DOI: https://doi.org/10.3321/j.issn:1002-185x.2006.z2.041
2006-01-01
Rare Metal Materials and Engineering
Abstract:The conventional solid-state technique was utilized to modify hydrotherrmally-synthesized-BaTiO3 with La2O3 and MgO. Sintering characteristic, dielectric properties, phases and microstructure of (Ba1-xLax)(Ti1-x/2Mgx/2)O-3 ceramics were studied in this paper. With the increase of composition x, the sintering temperature increased and the crystal structure changed from the tetragonal to the cubic. when x=0.0025, the substitution of Ti4+ for Mg2+ was significant, and the lattice parameter was increased. However, when x >= 0.2, the substitution of Ba for La3+ was significant, and the lattice parameter decreased. Grains size decreased with the increase of composition. When x=0.4, the average grain size was about 0.33 mu m, and the sample with compact and uniform microstructure was obtained. With the increase of composition x, the curie point was moved to room temperature and the epsilon(r) peak was widened and resistivity increased. Where x >= 0.2, dielectric constant increased and TCC decreased with the increase of composition x.