Abstract:Mn 0.6 Cu 0.2 Zn 0.2 O (Fe 2O 3) 0.98 (MnCuZn) ferrite powders with particle size about 30 nm were directly synthesized by sol-gel auto_combustion method at room temperature. The thermal decomposition, nature of auto_combustion and magnetic properties of the obtained powders were investigated by DTA-TG, IR, XRD and VSM techniques. The results revealed that xerogel derived from the nitrate-citrate exhibit auto_combustion behavior once ignited in air at room temperature. The nature of auto_combustion is considered to be an oxidation_reduction process induced by heat. The results of XRD indicates that pure nanocrystalline Mn 0.6 Cu 0.2 Zn 0.2 O(Fe 2O 3) 0.98 ferrite can be directly obtained after auto_combustion without further calcination and no phase of Fe 2O 3 is detected. The phase of Fe 2O 3 would appear when the auto_combustion powders were calcined at increasing temperature. The coercive force of MnCuZn ferrite powders is linearly decreased from 9.039 5 kA·m -1 (for auto_combustion powders) to 4.724 6 kA·m -1 (for auto_combustion powders calcined at 1 000 ℃ for 2 h) while the calcined temperature increases. However, the values of saturation magnetization firstly decrease, then increase with an increase in calcined temperature. The coercive force and saturation magnetization, of obtained nanosize MnCuZn ferrite powders are high as compared to reported bulk values.

Low Temperature Sol-gel Autocombustion Synthesis and Magnetic Properties of Magnetite

Synthesis of Nanocrystalline Ferrites Zn0.4ni0.6cr0.5laxfe1.5-Xo4 and Its Magnetic Properties

Synthesis of Monodispersed Fe3O4 Magnetite Nanoparticles by ethylene glycol solvothermal method

A Simple Solution Route to Control Synthesis of Fe3O4 Nanomaterials at Low Temperature and Their Magnetic Properties

Large Low-Field Magnetoresistance in Nanocrystalline Magnetite Prepared by Sol-Gel Method

Low Temperature Synthesis of Vanadium Pentoxide Nanocrystallines by Sol-Gel Method

Systematic Study on the Synthesis and Magnetism Properties of Manganese Ferrite MnFe2O4 by an Oxidation Roasting Process

Solvothermal Synthesis and Magnetic Property of Monodispersed Fe_3O_4 Nano-powders

SYNTHESIS OF NANOCRYSTALLINE Mn_(0.6)Cu_(0.2)Zn_(0.2)O(Fe_2O_3)_(0.98) FERRITE BY SOL-GEL AUTO-COMBUSTION METHOD AND CHARACTERIZATION OF ITS MAGNETIC PROPERTIES

Synthesis and characterization of magnetite nanoparticles by a simple solvothermal method

Sol–gel Autocombustion Synthesis and Characterization of Fe1−xCox Alloys with Large Saturation Magnetization

Room Temperature Preparation of Nanocrystalline MnCuZn Ferrite Powder by Auto-Combustion of Nitrate-Citrate Gels

Preparation of low-temperature sintered Mn doped Mg-Cu-Zn ferrites by sol-gel self-combustion method

Porous Fe3O4 and gamma-Fe2O3 foams synthesized in air by sol-gel autocombustion

Effect of Precursor Solutions with Different Composition on Synthesis of Ultrafine BaLa0.3Fe11.7O19using Sol-Gel Auto-Combustion Technique

Synthesis Of Nicuzn Ferrite Nano-Sized Particles By Sol-Gel Auto-Combustion

Auto-combustion synthesis of nanocrystalline LaFeO3

Low-density nanoporous iron foams synthesized by sol-gel autocombustion

Chemical Synthesis and Magnetic Study of Nanocrystalline Thin Films of Cobalt Spinel Ferrites

Characteristic of hydrothermal or Sol-Gel synthesized Mn0.8 Zn0.2Fe2O4 magnetic nano-materials

Synthesis of CoFe2O4 Nanoparticles via Solution Method and Their Magnetic Properties