Abstract:A low-cost and high-efficiency solid reaction method has been reported as an effective technology to synthesize manganese ferrite MnFe2O4 with a spinel crystal structure. This work clarified the underlying reason for the influence mechanism of SiO2 and Al2O3 on the synthesis of MnFe2O4. Synthetic MnFe2O4 polyhedral microparticles with a saturated magnetization of 71.19 emu/g, a ratio of saturation magnetization to residual magnetization (Ms/Mr) of 0.062 and a coercivity (Hc) of 6.50 Oe were successfully obtained at an oxidization roasting temperature of 1100 °C for 60 min. The experimental results indicate that the tetrahedral Mn2+ ions and octahedral Mn3+ ions in the crystal structure of manganese ferrite MnFe2O4 were replaced by tetrahedral Si2+ ions and octahedral Al3+ ions from (Mn2+)x(Fe2+)y(Si2+)1−x−y[Fe3+]2O4 and (Mn2+)[Fe3+]2−x[Al3+]xO4, respectively. In addition, hercynite FexMn1−xAl2O4 with a spinel crystal structure and olivine MnxFe2−xSiO4 with an orthorhombic crystal structure were partially formed in the synthesis of manganese ferrite MnFe2O4, in which some Fe2+ ions were easily replaced by Mn2+ ions to form stable hercynite MnAl2O4 and olivine Mn2SiO4 in these crystal structures. The current research work provides comprehensive insights for synthesizing manganese ferrite MnFe2O4 and continuously advances its technical progress.

Synthesis and characterization of magnetite nanoparticles by a simple solvothermal method

Synthesis of Monodispersed Fe3O4 Magnetite Nanoparticles by ethylene glycol solvothermal method

Solvothermal Synthesis and Magnetic Property of Monodispersed Fe_3O_4 Nano-powders

Solvothermal reduction synthesis and characterization of superparamagnetic magnetite nanoparticles

Magnetite Fe3O4 Nanoparticles and Hematite Α-Fe2o3 Uniform Oblique Hexagonal Microdisks, Drum-Like Particles and Spindles and Their Magnetic Properties

Polyol Synthesis of Superparamagnetic Fe_3O_4 Nanoparticles for Magnetic Resonance Imaging

A Simple Solution Route to Control Synthesis of Fe3O4 Nanomaterials at Low Temperature and Their Magnetic Properties

Preparation and characterization of Fe3O4 nanoparticles via a hydrothermal process with propanediol as the solvent

A facile two-step hydrothermal route for the synthesis of γ-Fe 2 O 3 nanocrystals and their magnetic properties

Synthesis of CoFe2O4 Nanoparticles via Solution Method and Their Magnetic Properties

Magnetite Nanostructures: One-pot Synthesis, Superparamagnetic Property and Application in Magnetic Resonance Imaging

Systematic Study on the Synthesis and Magnetism Properties of Manganese Ferrite MnFe2O4 by an Oxidation Roasting Process

Synthesis of Fe3O4 Nanoparticles and Their Magnetic Properties

Synthesis and Magnetic Properties of Mn-Zn Ferrite Nanoparticles

A simple solvothermal synthesis and characterization of round-biscuit-like Fe3O4 nanoparticles with adjustable sizes

Synthesis and Characterization of Monodisperse Fe3O4Nanospheres with Uniform Particle Size Distribution by a Simple Solvothermal Method

A Facile Solvothermal Synthesis of Octahedral Fe3 O4 Nanoparticles.

Synthesis and characterization of nano-sized magnetic ferroferric oxide particles

Synthesis of Nanometer-Size Maghemite Particles from Magnetite

Synthesis and characterization of thermo-sensitive magnetite-Au nanocomposites

Preparation of Water-Soluble Magnetite Nanocrystals Through Hydrothermal Approach