Abstract:Ductile iron contains free graphite nodules inside the metallic matrix, which generally consists of ferrite and pearlite in the as-cast condition. The casting thicknesses greatly influence on the size, shape, and quantity of the microconstituents of the metallic matrix and the graphite nodules and, therefore, on the mechanical properties. This investigation studied the cooling rate (imposed by the casting thicknesses) on the metallic matrix and the nodular characteristics of a ductile iron low alloyed with 0.8 %Ni and 0.15 %V. The ductile iron was manufactured by the sandwich technique with ladle inoculation. Six plates of different thicknesses, from 4.3 mm to 25.4 mm, were fabricated in a green sand mold. The microstructural characterization was performed by optical microscopy (OM), scanning electron microscopy (SEM), and the image J software by applying different quantification methods. The area method to obtain the average nodule size and nodularity provided more reliable results than the perimeter and total particle count methods. The hardness test on the Rockwell C scale carried out the mechanical characterization. The low content of vanadium added to the ductile cast iron had a negligible effect on the solidification pattern, mainly due to the graphitizing impact of the nickel and silicon addition. Thus, the microstructural features results are primarily due to the cooling rate imposed by the casting thickness. The thinnest casting section significantly improves the nodule count (414 Nod/mm2), sphericity (0.96), and nodularity (96.21 %). In contrast, the thickest casting plate obtained the highest volume fraction of graphite (10.85 %) and the lowest volume fraction of undesirable particles (0.36 %). The high cooling rate in the thinnest casting plate obtained the highest hardness of 31.56 HRC because of the higher contents of the volume fraction of pearlite (33.7 %) and carbides (4.5 %).

Effects of Antimony Addition and Section Size on Formation of Chunky Graphite in Ductile Iron

Effect of Sb on the Graphite Morphology and Mechanical Properties in Heavy Section Ductile Iron

Effects of Antimony on Structure and Properties of Vermiculate Cast Iron

Microstructure evolution of heavy section ductile iron

Graphite Morphology Evolution During Melt Holding of Ductile Iron

The Effect of Boron (B) and Copper (Cu) on the Microstructure and Graphite Morphology of Spheroidal Graphite Cast Iron

EFFECT OF Ce ON GRAPHITE NODULE COUNT AND SIZE DISTRIBUTION IN DUCTILE IRON

Effect of regular thicknesses on the microstructural and quantitative analysis for a hypo-eutectic ductile iron alloyed with Ni and V

Effects of graphite nodule count on mechanical properties and thermal conductivity of ductile iron

Examples of Chunky Graphite Formation in Production of Ductile Iron Castings and Effective Countermeasures

Wetting and Spreading Behavior of Molten Iron in Contact with Graphite Substrate: Interfacial Effects

Vermicular and Chunky Graphite Nucleation during Chill Casting: Study on the Dynamics of Ductile Iron Recycling

Effect of Purifying Agent on the Microstructure and Mechanical Properties of Nodular Graphite Cast Iron

Effects of Manganese and Heat Treatment on Mechanical Properties in Spheroidal Graphite Cast Iron

Effects of Titanium, Cerium or Aluminum Addition on Microstructure and Mechanical Properties of Ductile Iron Castings

Scanning Auger Microprobe Study of Interfacial Adsorption Behaviour of Some Minor Elements in Spheroidal-graphite Cast Iron

Relationships Between Macrostructure and Microstructure in Lamellar Graphite Iron Castings

The Influence Of Cast Structure On The Austempering Of Ductile Iron. Part 3. The Role Of Nodule Count On The Kinetics, Microstructure And Mechanical Properties Of Austempered Mn Alloyed Ductile Iron

Effects of Foundry Variables and Refiners on Cast Structures of Superalloy K4169ii. Dendrite Structures and Granulation Mechanisms

Modeling of Stable and Metastable Eutectic Transformation of Spheroidal Graphite Iron Casting.

Effect of Nb Addition on Compact Microstructure and Mechanical Properties of Gray Cast Iron for Cylinder Liner