Effects of Manganese and Heat Treatment on Mechanical Properties in Spheroidal Graphite Cast Iron

Tohru Nobuki,Takanori Aoki,Minoru Hatate

DOI: https://doi.org/10.1007/s40962-024-01389-3

2024-06-14

International Journal of Metalcasting

Abstract:It is well known that the mechanical properties of spheroidal graphite cast iron deeply depend on the volume of pearlite matrix microstructures. Therefore, the theoretical criterion of pearlite matrix nucleation is considered important in this graphite cast iron that to obtain the higher mechanical properties of graphite cast iron, the pearlite stabilizing element such as Mn or Cu is very important. The present work aims to study the influence of manganese (Mn) content and heat treatment on the mechanical properties of 3% or 4% (Solution Strengthened Ferritic Ductile Iron-SSFDI) of silicon (Si) containing spheroidal graphite cast irons. The six 3.6%C–3%Si melts with different chemical compositions from 0.2 to 1.7 mass% of Mn content were produced using a high-frequency induction furnace. The melt was poured into a Y-block CO 2 sand mold of 25 or 40 mm in thickness. The microstructure analysis and mechanical testing were performed for as-cast and some heat treatment conditions, such as annealing or air cooling. As a result, the tensile strength had a good relationship with the area fraction of pearlite, over 600 MPa in UTS, and high proof stress for some 3 or 4%Si–Mn series samples in the as-cast condition. By the heat treatment from the unique ( α + γ ) region, the 3% Si sample showed over 800 MPa and over 10% in elongation. And 4%Si–1.5%Mn (SSFDI) series sample showed over 600 MPa in UTS and over 15% in elongation which was prepared by annealing heat treatment to reduce to less than 5% of the area fraction of pearlite. This study suggests that it can be understood of the correlation between optimizing the heat treatment condition and mechanical properties of SSFDI cast irons.

metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper primarily investigates the effects of manganese (Mn) content and heat treatment on the mechanical properties of ductile iron containing 3% or 4% silicon (Si). Specifically, the research aims to:

1. **Effect of Manganese Content**: Study the impact of different manganese contents (ranging from 0.2% to 1.7%) on the mechanical properties of ductile iron containing 3% or 4% silicon.
2. **Effect of Heat Treatment**: Explore how different heat treatment conditions (such as annealing or air cooling) affect the mechanical properties of these iron materials.

The research background indicates that ductile iron is widely used in automotive applications as structural materials and high-load components due to its good machinability and relatively low cost. To enhance the strength and toughness of ductile iron, researchers have attempted to improve its performance by adding alloying elements, heat treatment, and processing methods. In particular, manganese, as an alloying element that promotes pearlite stability, is considered crucial for improving the mechanical properties of ductile iron.

The experimental section describes in detail the process of preparing samples with different manganese and silicon contents, and conducts microstructure analysis and mechanical testing. The research results show that with the increase in manganese content, the proportion of the pearlitic matrix increases, leading to higher tensile strength but decreased ductility; while the increase in silicon content tends to form a ferritic matrix, which helps improve ductility. Additionally, specific heat treatment conditions can significantly enhance the mechanical properties of the material. For example, for the 4% silicon series samples, annealing heat treatment can achieve high ductility (over 15%) while maintaining high tensile strength (over 600 MPa).

In summary, this paper aims to explore the effects of manganese content and heat treatment on the mechanical properties of ductile iron with specific silicon content, providing a theoretical basis for optimizing the performance of such materials.