Influence of Maximum Temperature on Thermal Fatigue Resistance of High Silicon-Molybdenum Vermicular Graphite Cast Iron

CHEN Dan,QIN Xian-feng,YAN Ming-hui,LI Li-lin,SANG Wei-wei

DOI: https://doi.org/10.3969/j.issn.1001-4977.2018.06.013

2018-01-01

Abstract:By the optical microscope (OM) and scanning electron microscope (SEM), the microstructures and thermal fatigue resistance of the high silicon-molybdenum vermicular graphite cast iron under various thermal cycle maximum temperature Tmax(600℃, 700℃, 800℃ and 900℃) were studied. The results show that with Tmax increasing, the pearlite and (FeMo)3C in the vermicular graphite cast iron disappear faster, and the residual (FeMo)3C significantly promotes the formation of thermal fatigue cracks. With increasing Tmax, the thermal fatigue resistance of the vermicular graphite cast iron decreases and the crack propagation mode changes. When Tmax=600-800℃, the propagating route of the main crack in the vermicular graphite cast iron is preferably along the long axis of the vermicular graphite, simultaneously connecting the ductile graphite or (FeMo)3C carbides which cause cracks initiated along the main crack. When Tmax=900℃, the main crack propagating paths are both along the long axis of vermicular graphite and along the vertical direction to widen the crack, connecting the spherical graphite by the way; since the crack band is relatively wider, the thermal fatigue resistance of the vermicular graphite cast iron deteriorates sharply.