Abstract:The purpose of the investigations was to study systematically the effects of different tempering temperatures on the microstructure, hardness and wear resistance of low‐silicon hypereutectic high‐chromium cast iron. It is expected to provide theoretical support for the development of tempering processes for this material. High‐chromium cast iron is a good wear‐resistant material. Its heat treatment regime has an important influence on the evolution of its microstructure and properties. This study investigates the microstructural attributes and properties of Fe–4.0 C–35.0Cr–0.5Si (wt.%) low‐silicon hypereutectic high‐chromium cast iron subsequent to quenching at 1050 °C, followed by tempering at diverse temperatures. The microstructure was examined using optical microscopy, scanning electron microscopy, and X‐ray diffractometry across varied tempering conditions. Furthermore, microhardness and wear resistance were conducted via a microhardness tester and a wear testing machine. The results show that the quenching heat treatment promotes the transformation of the matrix from austenite to martensite, while also promoting the precipitation of secondary carbides of M23C6‐type. The subsequent tempering heat treatment engenders transformations involving retained austenite to martensite, amplifies the precipitation and enlargement of secondary carbides, and induces martensite decomposition. As the tempering temperature increases, primary and eutectic carbides exhibit minimal changes, while the secondary carbide morphology evolves from granular to reticular. The matrix composition predominantly comprises martensite, interspersed with a minor fraction of austenite. It is worth noting that the alloy has the highest hardness and wear resistance after quenching at 1050 °C and then tempering at 400 °C.

Microstructure and Properties of Hypereutectic High Chromium White Cast Iron Prepared under Pressure

Microstructure and Properties of Semisolid Hypereutectic High Chromium Cast Iron Prepared by Slope Cooling Body Method

Preparation of Semisolid Hypereutectic High Chromium Cast Iron and Quantitative Analysis of Microstructure

Solidification Microstructure of Hypereutectic High Chromium Cast Iron Semi-solid Slurry in Centrifugal Casting

Effect of fluctuation and modification on microstructure and impact toughness of 20 wt.% Cr hypereutectic white cast iron

Characterization of Microstructure and Mechanical Properties of High Chromium Cast Irons Using Sem and Nanoindentation

Effect of Partial Remelting Temperature on Primary Phase in Semisolid Microstructure of Hypereutectic High Cr White Cast Iron

Effect of quenching temperature on microstructure and properties of low silicon hypereutectic high chromium cast iron

Effect of Heat Treatment on Microstructure and Mechanical Properties of a Ti-bearing Hypereutectic High Chromium White Cast Iron

Effect of Boron on the Microstructure and Properties of Semisolid Hypereutectic High Chromium Cast Iron

Microstructure Evolution and Properties of Nitrogen-Bearing Hypereutectic High Chromium Cast Iron after Quenching

Effect of Si on Microstructure and Wear Resistance of Hypereutectic High-Chromium Cast Iron

Effect of tempering temperature on microstructure and properties of low silicon hypereutectic high chromium cast ironAuswirkung der Anlasstemperatur auf das Gefüge und die Eigenschaften von übereutektischem Gusseisen mit niedrigem Siliziumgehalt und hohem Chromgehalt

Influence of Tungsten on Microstructure and Properties of As-Cast Hi-Cr Cast Iron

The characterization of porosity and externally solidified crystals in a high pressure die casting hypoeutectic Al-Si alloy using a newly developed ceramic shot sleeve

Microscopic Study of Carbide Precipitation during Heat Treatment of 35Cr–4C High Chromium Cast Iron

Solidification structure of C2.08Cr25.43Si1.19Mn0.43Fe70.87 powders fabricated by high pressure gas atomization

Effect of partial remelting time on the initial carbide in semisolid structure of hypereutectic hih Cr cast iron

Effect of TiC Particle Additions on Structure and Properties of Hypereutectic High Chromium Cast Iron

Preparation and Properties of ZTA + WC Particles/Hypereutectic High Chromium Cast Iron Composites

Effect of Fluctuation, Modification and Surface Chill on Structure of 20%cr Hypereutectic White Cast Iron