Abstract:The purpose of the investigations was to study systematically the effects of different tempering temperatures on the microstructure, hardness and wear resistance of low‐silicon hypereutectic high‐chromium cast iron. It is expected to provide theoretical support for the development of tempering processes for this material. High‐chromium cast iron is a good wear‐resistant material. Its heat treatment regime has an important influence on the evolution of its microstructure and properties. This study investigates the microstructural attributes and properties of Fe–4.0 C–35.0Cr–0.5Si (wt.%) low‐silicon hypereutectic high‐chromium cast iron subsequent to quenching at 1050 °C, followed by tempering at diverse temperatures. The microstructure was examined using optical microscopy, scanning electron microscopy, and X‐ray diffractometry across varied tempering conditions. Furthermore, microhardness and wear resistance were conducted via a microhardness tester and a wear testing machine. The results show that the quenching heat treatment promotes the transformation of the matrix from austenite to martensite, while also promoting the precipitation of secondary carbides of M23C6‐type. The subsequent tempering heat treatment engenders transformations involving retained austenite to martensite, amplifies the precipitation and enlargement of secondary carbides, and induces martensite decomposition. As the tempering temperature increases, primary and eutectic carbides exhibit minimal changes, while the secondary carbide morphology evolves from granular to reticular. The matrix composition predominantly comprises martensite, interspersed with a minor fraction of austenite. It is worth noting that the alloy has the highest hardness and wear resistance after quenching at 1050 °C and then tempering at 400 °C.

Effect of fluctuation and modification on microstructure and impact toughness of 20 wt.% Cr hypereutectic white cast iron

Microscopic Study of Carbide Precipitation during Heat Treatment of 35Cr–4C High Chromium Cast Iron

Influence of Tungsten on Microstructure and Properties of As-Cast Hi-Cr Cast Iron

Effect of aluminum on the primary carbides of a hypereutectic high chromium cast iron

Effect of Carbon and Cooling Rate on the Structure of Hypereutectic High Chromium Cast Iron in the Cast State and after Heat Treatment

Effect of tempering temperature on microstructure and properties of low silicon hypereutectic high chromium cast ironAuswirkung der Anlasstemperatur auf das Gefüge und die Eigenschaften von übereutektischem Gusseisen mit niedrigem Siliziumgehalt und hohem Chromgehalt

Investigation of microstructure evolution and mechanical properties of near-eutectic Fe2-CoNiCr C high entropy cast iron

Effect of quenching temperature on microstructure and properties of multivariate high chromium cast iron

Effect of quenching temperature on microstructure and properties of low silicon hypereutectic high chromium cast iron

Simulation of the Kinetics of Microstructure Evolution during Destabilization and Tempering of a High-Chromium White Cast Iron

Effect of Chromium Content on Microstructure, Hardness, and Wear Resistance of As-Cast Fe-Cr-B Alloy

Microstructure Evolution and Properties of Nitrogen-Bearing Hypereutectic High Chromium Cast Iron after Quenching

Refinement of primary carbides in hypereutectic high-chromium cast irons: a review

Modification and refinement of Fe-containing phases, mechanical properties and strengthening mechanisms in Al–Fe alloys via Cr alloying and continuous rheo-extrusion

Characterization of Microstructure and Mechanical Properties of High Chromium Cast Irons Using Sem and Nanoindentation

Effect of Chromium Content on Heat Treatment Behavior of Multi-Alloyed White Cast Iron for Abrasive Wear Resistance

Microstructure and Mechanical Properties of High Boron White Cast Iron with about 4 Wt% Chromium

Effect of Si on Microstructure and Wear Resistance of Hypereutectic High-Chromium Cast Iron

Tempering temperature dependence on the microstructure, mechanical properties and wear behaviour of a novel high chromium cast iron

Influence of Heat Treatment on Erosive Wear Resistance of High Cr Cast Irons

Corrosion Wear of Hypereutectic High Chromium Cast Iron: A Review