Abstract:The purpose of the investigations was to study systematically the effects of different tempering temperatures on the microstructure, hardness and wear resistance of low‐silicon hypereutectic high‐chromium cast iron. It is expected to provide theoretical support for the development of tempering processes for this material. High‐chromium cast iron is a good wear‐resistant material. Its heat treatment regime has an important influence on the evolution of its microstructure and properties. This study investigates the microstructural attributes and properties of Fe–4.0 C–35.0Cr–0.5Si (wt.%) low‐silicon hypereutectic high‐chromium cast iron subsequent to quenching at 1050 °C, followed by tempering at diverse temperatures. The microstructure was examined using optical microscopy, scanning electron microscopy, and X‐ray diffractometry across varied tempering conditions. Furthermore, microhardness and wear resistance were conducted via a microhardness tester and a wear testing machine. The results show that the quenching heat treatment promotes the transformation of the matrix from austenite to martensite, while also promoting the precipitation of secondary carbides of M23C6‐type. The subsequent tempering heat treatment engenders transformations involving retained austenite to martensite, amplifies the precipitation and enlargement of secondary carbides, and induces martensite decomposition. As the tempering temperature increases, primary and eutectic carbides exhibit minimal changes, while the secondary carbide morphology evolves from granular to reticular. The matrix composition predominantly comprises martensite, interspersed with a minor fraction of austenite. It is worth noting that the alloy has the highest hardness and wear resistance after quenching at 1050 °C and then tempering at 400 °C.

Preparation of Semisolid Hypereutectic High Chromium Cast Iron and Quantitative Analysis of Microstructure

Microstructure and Properties of Semisolid Hypereutectic High Chromium Cast Iron Prepared by Slope Cooling Body Method

Effect of partial remelting time on the initial carbide in semisolid structure of hypereutectic hih Cr cast iron

Microstructure and Properties of Hypereutectic High Chromium White Cast Iron Prepared under Pressure

Solidification Microstructure of Hypereutectic High Chromium Cast Iron Semi-solid Slurry in Centrifugal Casting

Effect of Partial Remelting Temperature on Primary Phase in Semisolid Microstructure of Hypereutectic High Cr White Cast Iron

Effect of Fluctuation, Modification and Surface Chill on Structure of 20%cr Hypereutectic White Cast Iron

Effect of fluctuation and modification on microstructure and impact toughness of 20 wt.% Cr hypereutectic white cast iron

Microscopic Study of Carbide Precipitation during Heat Treatment of 35Cr–4C High Chromium Cast Iron

Effect of quenching temperature on microstructure and properties of low silicon hypereutectic high chromium cast iron

Effects of Fluctuation Modification on As-cast Microstructure of Hypereutectic White Cast Iron

Effect of Boron on the Microstructure and Properties of Semisolid Hypereutectic High Chromium Cast Iron

Effect of quenching temperature on microstructure and properties of multivariate high chromium cast iron

Improvement to the Morphology of Carbides in Low Alloy White Cast Iron

Effect of tempering temperature on microstructure and properties of low silicon hypereutectic high chromium cast ironAuswirkung der Anlasstemperatur auf das Gefüge und die Eigenschaften von übereutektischem Gusseisen mit niedrigem Siliziumgehalt und hohem Chromgehalt

Influences of Si/C Ratio and Speed of Cooling on the Structure and Properties of Medium-chromium Cast Iron As-cast

Investigation of microstructure evolution and mechanical properties of near-eutectic Fe2-CoNiCr C high entropy cast iron

Characterization of Microstructure and Mechanical Properties of High Chromium Cast Irons Using Sem and Nanoindentation

Microstructure evolution of heavy section ductile iron

Microstructure Evolution and Properties of Nitrogen-Bearing Hypereutectic High Chromium Cast Iron after Quenching

Effect of TiC Particle Additions on Structure and Properties of Hypereutectic High Chromium Cast Iron