Abstract:High chromium cast iron (HCCI) is widely used in mining and metallurgy due to its high wear resistance. The purpose of this study is to reveal the effects of different quenching temperatures on the microstructure evolution, hardness and wear resistance of nitrogen-containing hypereutectic high chromium cast iron (HHCCI). The results show that with the increase of quenching temperature, the primary carbides change from hexagonal prism to irregular shape, and the eutectic carbides change from daisy-like and strip-like to larger lumps with a tendency to aggregate and grow. The secondary carbides are mainly transformed from precipitation to re-dissolution, and there are two morphologies of the precipitated secondary carbides. One is block, which is mainly M 7 C 3 type and distributed around primary and eutectic carbides by TEM analysis. The other is short rod-like, of the M 23 C 6 type, which tends to precipitate in the "central" region far away from the eutectic carbide. With the increase of quenching temperature, the hardness and wear resistance of hypereutectic high chromium cast iron show a tendency of increasing first and then decreasing, and quenching at 1050 °C, the specimen shows the highest hardness of 66.0 HRC and the best wear resistance. It was expected to provide reference for the formulation of heat treatment quenching process of nitrogen-containing HHCCI.

Microstructure and Properties of Semisolid Hypereutectic High Chromium Cast Iron Prepared by Slope Cooling Body Method

Preparation of Semisolid Hypereutectic High Chromium Cast Iron and Quantitative Analysis of Microstructure

Solidification Microstructure of Hypereutectic High Chromium Cast Iron Semi-solid Slurry in Centrifugal Casting

Microstructure and Properties of Hypereutectic High Chromium White Cast Iron Prepared under Pressure

Effect of fluctuation and modification on microstructure and impact toughness of 20 wt.% Cr hypereutectic white cast iron

Effect of Boron on the Microstructure and Properties of Semisolid Hypereutectic High Chromium Cast Iron

Influence of Tungsten on Microstructure and Properties of As-Cast Hi-Cr Cast Iron

Effect of Fluctuation, Modification and Surface Chill on Structure of 20%cr Hypereutectic White Cast Iron

Effect of partial remelting time on the initial carbide in semisolid structure of hypereutectic hih Cr cast iron

Microscopic Study of Carbide Precipitation during Heat Treatment of 35Cr–4C High Chromium Cast Iron

Effect of quenching temperature on microstructure and properties of low silicon hypereutectic high chromium cast iron

Effect of Partial Remelting Temperature on Primary Phase in Semisolid Microstructure of Hypereutectic High Cr White Cast Iron

Investigation of microstructure evolution and mechanical properties of near-eutectic Fe2-CoNiCr C high entropy cast iron

Microstructure Evolution and Properties of Nitrogen-Bearing Hypereutectic High Chromium Cast Iron after Quenching

Characterization of Microstructure and Mechanical Properties of High Chromium Cast Irons Using Sem and Nanoindentation

Study on Influence of Surface Coating During Cooling Slope Rheocasting Process

Effect of TiC Particle Additions on Structure and Properties of Hypereutectic High Chromium Cast Iron

Effect of Titanium on the As-Cast Microstructure of Hypereutectic High Chromium Cast Iron

Effects of Quenching Medium on Microstructure and Mechanical Properties of High Chromium Cast Iron

Effects of Fluctuation Modification on As-cast Microstructure of Hypereutectic White Cast Iron

Effect of Cr Content on the Microstructure of Casting Infiltration Layers: Simulations and Experiments