Abstract:This study investigates the kinetics of microstructure development during the solidification and heat treatment processes of a white iron with 19 wt.% Cr. For this purpose, the as-cast microstructure with large eutectic carbides in austenite quantified by Scheil–Gulliver simulation and experimental studies was used as input for the precipitation kinetics simulations of destabilization and tempering heat treatments. Simulations showed that during the heating stage of destabilization, M 7 C 3 and M 23 C 6 secondary carbides nucleated and grew together. With increased temperature, it was observed that M 23 C 6 dissolved completely and M 7 C 3 reached a self-similar size distribution. During isothermal holding, secondary M 7 C 3 carbides coarsened. Further, carbide precipitation in austenite was observed at the first 3 min of air quenching, and the total carbide volume fraction was found to increase by 26.4% at the end of destabilization. Subsequent tempering of the alloy at 450 °C led to precipitation of M 7 C 3 and M 23 C 6 tempered carbides in martensite and increased the total carbide volume fraction further by 5.3%. Similar to destabilization, it was observed that nucleation of these carbides took place during the heating stage of tempering. Although it requires further validation on a range of commercial high Cr white cast iron compositions and developments in regards to industrial heat treatment practice, agreement with the validation studies carried out in this work suggests that the presented modeling approach is useful for designing white cast iron alloys for better performance by optimizing the microstructure through heat treatment processing.

Effects of Fluctuation Modification on As-cast Microstructure of Hypereutectic White Cast Iron

Effect of Fluctuation, Modification and Surface Chill on Structure of 20%cr Hypereutectic White Cast Iron

Effect of fluctuation and modification on microstructure and impact toughness of 20 wt.% Cr hypereutectic white cast iron

Microscopic Study of Carbide Precipitation during Heat Treatment of 35Cr–4C High Chromium Cast Iron

Effect of titanium on the microstructure of hypereutectic high-chromium cast iron

Influence of Tungsten on Microstructure and Properties of As-Cast Hi-Cr Cast Iron

Effect of Carbon and Cooling Rate on the Structure of Hypereutectic High Chromium Cast Iron in the Cast State and after Heat Treatment

Manufacture and Microstructures of Fe-Cr-C Hypereutectic In Situ Composites

Effect of aluminum on the primary carbides of a hypereutectic high chromium cast iron

Effect of partial remelting time on the initial carbide in semisolid structure of hypereutectic hih Cr cast iron

Preparation of Semisolid Hypereutectic High Chromium Cast Iron and Quantitative Analysis of Microstructure

Effect of TiC Particle Additions on Structure and Properties of Hypereutectic High Chromium Cast Iron

Effect of quenching temperature on microstructure and properties of multivariate high chromium cast iron

Effect of Titanium on the As-Cast Microstructure of Hypereutectic High Chromium Cast Iron

Effect of Heat Treatment on Microstructure and Mechanical Properties of a Ti-bearing Hypereutectic High Chromium White Cast Iron

Simulation of the Kinetics of Microstructure Evolution during Destabilization and Tempering of a High-Chromium White Cast Iron

Influence of Cooling Rate After Destabilization on Microstructure and Hardness of a High-Cr Cast Iron

Refining Effect of Nb on Hypereutectic High-Chromium Cast Iron

Refining Mechanism of Ti on Hypereutectic High-Chromium Cast Iron

Understanding Effects of Cr Content on the Slurry Erosion Behavior of High-Cr Cast Irons Through Local Property Mapping and Computational Analysis

Solidification Microstructure of Hypereutectic High Chromium Cast Iron Semi-solid Slurry in Centrifugal Casting